	Constitutive flow behaviour and finite element simulation of hot rolling of SiCp/2009A1 composite
	Zhou, L.; Huang, Z. Y.; Wang, C. Z.; Zhang, X. X.; Xiao, B. L.; Ma, Z. Y.; zyma@imr.ac.cn
	2016
发表期刊	MECHANICS OF MATERIALS
ISSN	0167-6636
卷号	93 页码:32-42
摘要	The material parameters of 17vol.%SiCp/2009Al composite in the Arrhenius-type constitutive equations were calculated using experimental data from hot compression tests. The constitutive equation was then implemented into the finite element software, ABAQUS/Explicit, to calculate the stress, deformation and edge damage in the hot rolling process. The initiation and propagation of edge cracks under the hot rolling condition were studied via the Gurson-Tvergaard-Needleman (GTN) damage model. The influence of the thickness reduction on the strip damage was assessed. The results indicate that the high tensile stress at the edge of the strip causes crack initiation and propagation, and the total reduction has a significant effect on the damage in the hot rolling of the SiCp/2009Al composites. When the reduction is less than 20%, no crack initiates and the damage occurs on the strip surface. With increase of the total reduction to 25% and larger, edge cracks occur and increase gradually. The distribution and direction of edge cracks are closely correlated with the stress components. The hot rolling experiments on 17vol.%SiCp/2009Al composite were conducted to evaluate the simulation results, and it is indicated that the finite element calculation results agreed well with the experimental results. This indicates that the finite element analysis is able to successfully simulate the rolling process and provide important information for the process optimization. (C) 2015 Elsevier Ltd. All rights reserved.
部门归属	[zhou, l. ; huang, z. y. ; zhang, x. x. ; xiao, b. l. ; ma, z. y.] chinese acad sci, inst met res, shenyang 110016, peoples r china ; [zhou, l. ; wang, c. z.] shenyang ligong univ, sch mech engn, shenyang 110159, peoples r china
关键词	Composites Constitutive Modelling Hot Rolling Finite Element Simulation
资助者	National Basic Research Program of China [2012CB619600]
收录类别	sci
语种	英语
WOS记录号	WOS:000368748900003
引用统计	被引频次：26[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/74681
专题	中国科学院金属研究所
通讯作者	zyma@imr.ac.cn
推荐引用方式 GB/T 7714	Zhou, L.,Huang, Z. Y.,Wang, C. Z.,et al. Constitutive flow behaviour and finite element simulation of hot rolling of SiCp/2009A1 composite[J]. MECHANICS OF MATERIALS,2016,93:32-42.
APA	Zhou, L..,Huang, Z. Y..,Wang, C. Z..,Zhang, X. X..,Xiao, B. L..,...&zyma@imr.ac.cn.(2016).Constitutive flow behaviour and finite element simulation of hot rolling of SiCp/2009A1 composite.MECHANICS OF MATERIALS,93,32-42.
MLA	Zhou, L.,et al."Constitutive flow behaviour and finite element simulation of hot rolling of SiCp/2009A1 composite".MECHANICS OF MATERIALS 93(2016):32-42.