Effect of different processes on lamellar-free ultrafine grain formation, room temperature superplasticity and fracture mode of Zn-22Al alloy
Demirtas, M.; Purcek, G.; Yanar, H.; Zhang, Z. J.; Zhang, Z. F.; purcek@ktu.edu.tr
2016
Source PublicationJOURNAL OF ALLOYS AND COMPOUNDS
ISSN0925-8388
Volume663Pages:775-783
AbstractThe Zn-22 wt.% Al was processed using five different selected routes including thermal, thermomechanical and severe plastic deformation (SPD) techniques in order to produce ultrafine grained (UFG) microstructure for achieving room temperature (RT) and high strain rate (HSR) superplasticity, and to compare the same set of the results. After all routes, the microstructural evolutions and RT uniaxial tensile tests at different strain rates ranging from 1 x 10(-3) to 1 x 10(0) s(-1) were investigated. The smallest grain size was achieved to be 300 nm after the thermo-mechanical process including conventional hot and cold rolling steps. However, the lamellar microstructure of the alloy was not completely eliminated during that process. On the other hand, equal-channel angular pressing (ECAP) as one of the SPD techniques decreased the grain size down to 400 nm with a lamellar-free microstructure. The maximum elongation value was achieved to be 330% with the sample tested at 1 x 10(-3) s(-1) after a thermomechanical process including conventional hot and cold rolling, and an aging stage between these rolling steps. It was found that lamellar-free microstructure causes higher superplastic elongation even if it has higher grain size compared to the sample having partially lamellar structure. (C) 2015 Elsevier B.V. All rights reserved.
description.department[demirtas, m.] bayburt univ, dept mech engn, tr-69000 bayburt, turkey ; [purcek, g. ; yanar, h.] karadeniz tech univ, dept mech engn, tr-61080 trabzon, turkey ; [zhang, z. j. ; zhang, z. f.] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china
KeywordZn-22al Alloy Superplasticity Ufg Materials Severe Plastic Deformation
Funding OrganizationScientific Research Projects of Karadeniz Technical University, Turkey [10501]
Indexed Bysci
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/74744
Collection中国科学院金属研究所
Corresponding Authorpurcek@ktu.edu.tr
Recommended Citation
GB/T 7714
Demirtas, M.,Purcek, G.,Yanar, H.,et al. Effect of different processes on lamellar-free ultrafine grain formation, room temperature superplasticity and fracture mode of Zn-22Al alloy[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2016,663:775-783.
APA Demirtas, M.,Purcek, G.,Yanar, H.,Zhang, Z. J.,Zhang, Z. F.,&purcek@ktu.edu.tr.(2016).Effect of different processes on lamellar-free ultrafine grain formation, room temperature superplasticity and fracture mode of Zn-22Al alloy.JOURNAL OF ALLOYS AND COMPOUNDS,663,775-783.
MLA Demirtas, M.,et al."Effect of different processes on lamellar-free ultrafine grain formation, room temperature superplasticity and fracture mode of Zn-22Al alloy".JOURNAL OF ALLOYS AND COMPOUNDS 663(2016):775-783.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Demirtas, M.]'s Articles
[Purcek, G.]'s Articles
[Yanar, H.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Demirtas, M.]'s Articles
[Purcek, G.]'s Articles
[Yanar, H.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Demirtas, M.]'s Articles
[Purcek, G.]'s Articles
[Yanar, H.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.