Effects of Sintering Method and Sintering Temperature on the Microstructure and Properties of Porous Y2SiO5
Wu, Zhen; Sun, Luchao; Wang, Jingyang; jywang@imr.ac.cn
2015
Source PublicationJOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
ISSN1005-0302
Volume31Issue:12Pages:1237-1243
AbstractPorous Y2SiO5 ceramic is a promising high-temperature thermal insulator in harsh environment. However, all the published relevant works faced serious problems, such as severe linear shrinkage, low porosity and low strength. In this study, porous Y2SiO5 ceramic with low sintering shrinkage and high porosity was successfully prepared by foam-gelcasting method using gelatin as the gelling agent. The effects of sintering methods, including in situ reaction sintering and direct sintering, and sintering temperatures on the phase composition, microstructure, shrinkage, porosity, and compressive strength of porous Y2SiO5 were investigated. Compared with samples fabricated by direct sintering, porous Y2SiO5 ceramic prepared via in situ reaction sintering method has the merits of the low linear shrinkage of 1.0%-4.7%, low bulk density of 0.79-0.88 g/cm(3), high porosity of 82.1%-80.1%, and high strength of 3.54-8.03 MPa, when the sintering temperatures increase from 1350 to 1550 degrees C. Porous Y2SiO5 has unique multiple pore structures, especially containing the interconnected small pores in skeleton. The thermal conductivity of porous Y2SiO5 is very low, which is 0.228 W/(m . K) for the sample with a porosity of 79.6%. This work reports an optimal processing method of highly porous Y2SiO5 with the potential application as high-temperature thermal insulation material. Copyright (C) 2015, The editorial office of Journal of Materials Science & Technology. Published by Elsevier Limited. All rights reserved.
description.department[wu, zhen] univ sci & technol china, hefei 230026, peoples r china ; [wu, zhen ; sun, luchao ; wang, jingyang] chinese acad sci, inst met res, shenyang natl lab mat sci, high performance ceram div, shenyang 110016, peoples r china
KeywordPorous Y2sio5 Ceramic In Situ Synthesis Mechanical Property Thermal Property
Funding OrganizationNational Natural Science Foundation of China [51032006, 51372252]
Indexed Bysci
Language英语
WOS IDWOS:000366158000012
Citation statistics
Cited Times:8[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/74793
Collection中国科学院金属研究所
Corresponding Authorjywang@imr.ac.cn
Recommended Citation
GB/T 7714
Wu, Zhen,Sun, Luchao,Wang, Jingyang,et al. Effects of Sintering Method and Sintering Temperature on the Microstructure and Properties of Porous Y2SiO5[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2015,31(12):1237-1243.
APA Wu, Zhen,Sun, Luchao,Wang, Jingyang,&jywang@imr.ac.cn.(2015).Effects of Sintering Method and Sintering Temperature on the Microstructure and Properties of Porous Y2SiO5.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,31(12),1237-1243.
MLA Wu, Zhen,et al."Effects of Sintering Method and Sintering Temperature on the Microstructure and Properties of Porous Y2SiO5".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 31.12(2015):1237-1243.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Wu, Zhen]'s Articles
[Sun, Luchao]'s Articles
[Wang, Jingyang]'s Articles
Baidu academic
Similar articles in Baidu academic
[Wu, Zhen]'s Articles
[Sun, Luchao]'s Articles
[Wang, Jingyang]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Wu, Zhen]'s Articles
[Sun, Luchao]'s Articles
[Wang, Jingyang]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.