Electrochemical Behavior of Zirconium in an in-situ Preparing LiCl-KCl-ZrCl4 Molten Slat

IMR OpenIR

	Electrochemical Behavior of Zirconium in an in-situ Preparing LiCl-KCl-ZrCl4 Molten Slat
	Cai, Yanqing; Liu, Hongxia; Xu, Qian; Song, Qiushi; Liu, Huijun; Xu, Liang; qianxu201@mail.neu.edu.cn
	2015
发表期刊	INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE
ISSN	1452-3981
卷号	10 期号:5 页码:4324-4334
摘要	The electrochemical behavior of zirconium was investigated in an in-situ preparing LiCl-KCl-ZrCl4 molten slat at 773 K by cyclic voltammetry, chronopotentiometry, and open circuit chronopotentiometry. The concentration of ZrCl4 in the salt is shown to have a great influence on the reduction process of zirconium. Two reduction steps at about -1.05 and -1.25 V due to Zr(IV)/Zr(II) and subsequently Zr(IV)/Zr and Zr(II)/Zr are observed at the lower concentration of ZrCl4 (0.28 wt.%). At the medium concentration of ZrCl4 (0.75 wt.% and 1.25 wt.%), another reduction step at -1.60 V corresponding to ZrCl/Zr is observed, indicating that Zr(IV) would reduce to ZrCl expecting for Zr at -1.25 V. What's more, the reduction of Zr(II) to ZrCl is also observed at -1.40 V at the higher concentration of ZrCl4 (1.80 wt.%). In the anodic dissolution process, Zr firstly oxidizes to Zr(II) and Zr(IV), and then Zr(II) further oxidizes to Zr(IV).
部门归属	[cai, yanqing ; liu, hongxia ; song, qiushi ; xu, liang] northeastern univ, sch mat sci & met, shenyang 110004, peoples r china ; [xu, qian] shanghai univ, sch mat sci & engn, shanghai 200072, peoples r china ; [liu, huijun] chinese acad sci, inst met res, lab corros & protect, shenyang 110016, peoples r china
关键词	Electrochemical Behavior Zirconium Licl-kcl Cyclic Voltammetry Chronopotentiometry
资助者	National Natural Science Foundation of China [51174055]
收录类别	sci
语种	英语
WOS记录号	WOS:000354782200054
引用统计	被引频次：11[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/74807
专题	中国科学院金属研究所
通讯作者	qianxu201@mail.neu.edu.cn
推荐引用方式 GB/T 7714	Cai, Yanqing,Liu, Hongxia,Xu, Qian,et al. Electrochemical Behavior of Zirconium in an in-situ Preparing LiCl-KCl-ZrCl4 Molten Slat[J]. INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,2015,10(5):4324-4334.
APA	Cai, Yanqing.,Liu, Hongxia.,Xu, Qian.,Song, Qiushi.,Liu, Huijun.,...&qianxu201@mail.neu.edu.cn.(2015).Electrochemical Behavior of Zirconium in an in-situ Preparing LiCl-KCl-ZrCl4 Molten Slat.INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,10(5),4324-4334.
MLA	Cai, Yanqing,et al."Electrochemical Behavior of Zirconium in an in-situ Preparing LiCl-KCl-ZrCl4 Molten Slat".INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE 10.5(2015):4324-4334.