Electrochemical study of the corrosion of a Ni-based alloy GH3535 in molten (Li,Na,K)F at 700 degrees C
Wang, Yanli; Liu, Huijun; Yu, Guojun; Hou, Juan; Zeng, Chaoliu; liuhj@imr.ac.cn
2015
Source PublicationJOURNAL OF FLUORINE CHEMISTRY
ISSN0022-1139
Volume178Pages:14-22
AbstractThe compatibility of structural materials with molten fluoride salts is an immediate challenge for the application and development of molten salt reactor (MSR) operating at high temperatures. In the present presentation, the corrosion behavior of a nickel-based alloy GH3535 has been examined in an eutectic (Li,Na,K)F melt at 700 degrees C under Ar and Ar-5%H2O, respectively, by some electrochemical techniques. Moreover, the effect of the additive CrF3 with concentrations of 0.09 and 0.18 M on the corrosion of the alloy in the melt has also been investigated in an attempt to understand the corrosion mechanism involving the multivalent transition metal Cr ions Cr2+/Cr3+. It is shown that the alloy is in active dissolution state at the corrosion potential and its corrosion occurs mainly through the preferential dissolution of Cr from the substrate, producing a Cr-depleted layer and some internal voids. The introduction of 5%H2O in Ar accelerates obviously the corrosion of the alloy, giving rise to the formation of a wider Cr-depleted layer where some Cr-rich internal oxides are formed over the internal voids. CrF3 itself acts as an oxidizer to accelerate the dissolution of Cr, with a more significant effectiveness observed for a higher CrF3 content. (C) 2015 Elsevier B.V. All rights reserved.
description.department[wang, yanli ; liu, huijun ; zeng, chaoliu] chinese acad sci, lab corros & protect, inst met res, shenyang 110016, peoples r china ; [yu, guojun ; hou, juan] chinese acad sci, shanghai inst appl phys, shanghai 201800, peoples r china
KeywordNi-based Alloy Gh3535 Molten Fluorides Corrosion Chromium Fluorides Electrochemical Techniques
Funding OrganizationNational Natural Science Foundation of China [51271190]
Indexed Bysci
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/74813
Collection中国科学院金属研究所
Corresponding Authorliuhj@imr.ac.cn
Recommended Citation
GB/T 7714
Wang, Yanli,Liu, Huijun,Yu, Guojun,et al. Electrochemical study of the corrosion of a Ni-based alloy GH3535 in molten (Li,Na,K)F at 700 degrees C[J]. JOURNAL OF FLUORINE CHEMISTRY,2015,178:14-22.
APA Wang, Yanli,Liu, Huijun,Yu, Guojun,Hou, Juan,Zeng, Chaoliu,&liuhj@imr.ac.cn.(2015).Electrochemical study of the corrosion of a Ni-based alloy GH3535 in molten (Li,Na,K)F at 700 degrees C.JOURNAL OF FLUORINE CHEMISTRY,178,14-22.
MLA Wang, Yanli,et al."Electrochemical study of the corrosion of a Ni-based alloy GH3535 in molten (Li,Na,K)F at 700 degrees C".JOURNAL OF FLUORINE CHEMISTRY 178(2015):14-22.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Wang, Yanli]'s Articles
[Liu, Huijun]'s Articles
[Yu, Guojun]'s Articles
Baidu academic
Similar articles in Baidu academic
[Wang, Yanli]'s Articles
[Liu, Huijun]'s Articles
[Yu, Guojun]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Wang, Yanli]'s Articles
[Liu, Huijun]'s Articles
[Yu, Guojun]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.