Enhancing mechanical properties of friction stir welded 2219Al-T6 joints at high welding speed through water cooling and post-welding artificial ageing
Zhang, Z.; Xiao, B. L.; Ma, Z. Y.; zyma@imr.ac.cn
2015
Source PublicationMATERIALS CHARACTERIZATION
ISSN1044-5803
Volume106Pages:255-265
AbstractThe effect of water cooling and post-welding artificial ageing on the microstructure and mechanical properties of 5.6-mm thick friction stir welded (FSW) 2219Al-T6 joints was subjected to detailed investigations. Sound FSW joints could be produced at the investigated welding speeds of 100-800 mm/min under both water-cooling and air-cooling conditions. The FSW thermal cycle resulted in a low hardness zone (LHZ) on both the retreating side and the advancing side. Water cooling did not exert an obvious effect on the hardness value and location of the LHZs but slightly improved the tensile strength of the FSW 2219Al-T6 joints at welding speeds of 100 and 400 mm/min. After post-welding artificial ageing, the hardness of LHZs and tensile strength of FSW 2219Al-T6 joints were substantially enhanced for all welding speeds and the strength increment increased with increases in the welding speed from 100 to 800 mm/min, attributable to increased precipitation of Al2Cu phases in both the LHZs and the nugget zone. A combination of high welding speed and post-welding artificial ageing is proven to be the optimal path to improving the mechanical properties of FSW 2219Al-T6 joints, with a maximum joint efficiency of 91% obtained. (C) 2015 Elsevier Inc. All rights reserved.
description.department[zhang, z. ; xiao, b. l. ; ma, z. y.] chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china
KeywordAluminium Alloys Friction Stir Welding Ageing Microstructure Mechanical Properties
Funding OrganizationNational Natural Science Foundation of China [51331008]
Indexed Bysci
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/74828
Collection中国科学院金属研究所
Corresponding Authorzyma@imr.ac.cn
Recommended Citation
GB/T 7714
Zhang, Z.,Xiao, B. L.,Ma, Z. Y.,et al. Enhancing mechanical properties of friction stir welded 2219Al-T6 joints at high welding speed through water cooling and post-welding artificial ageing[J]. MATERIALS CHARACTERIZATION,2015,106:255-265.
APA Zhang, Z.,Xiao, B. L.,Ma, Z. Y.,&zyma@imr.ac.cn.(2015).Enhancing mechanical properties of friction stir welded 2219Al-T6 joints at high welding speed through water cooling and post-welding artificial ageing.MATERIALS CHARACTERIZATION,106,255-265.
MLA Zhang, Z.,et al."Enhancing mechanical properties of friction stir welded 2219Al-T6 joints at high welding speed through water cooling and post-welding artificial ageing".MATERIALS CHARACTERIZATION 106(2015):255-265.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhang, Z.]'s Articles
[Xiao, B. L.]'s Articles
[Ma, Z. Y.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhang, Z.]'s Articles
[Xiao, B. L.]'s Articles
[Ma, Z. Y.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhang, Z.]'s Articles
[Xiao, B. L.]'s Articles
[Ma, Z. Y.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.