Short time oxidation behavior of 308L weld metal and 316L stainless steel with different surface state in simulated primary water with 0.1 mg/L dissolved oxygen

IMR OpenIR

	Short time oxidation behavior of 308L weld metal and 316L stainless steel with different surface state in simulated primary water with 0.1 mg/L dissolved oxygen
	Ming, H. -L.; Zhang, Z. -M.; Wang, S. -Y.; Wang, J. -Q.; Han, E. -H.; Ke, W.
	2015
发表期刊	MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION
ISSN	0947-5117
卷号	66 期号:9 页码:869-881
摘要	Many failures in nuclear safe-end dissimilar metal weld joint (DMWJ) have revealed that stress corrosion cracking (SCC) is mainly located in the weld metal (WM). Since the oxide film formed on the stainless steel during service plays an important role in SCC, this research focuses on the short time oxidation behavior of 308 L WM with different surface state in the simulated primary water of pressurized water reactors (PWRs) with 0.1 mg/L dissolved oxygen (DO). In the meanwhile, the oxidation behavior of the 316 L stainless steel with different surface state under the same environmental condition is also studied. Surface state and oxide films are analyzed using various methods. The results show that a dual layered oxide film is formed on 308L WM and 316 L surfaces. Both the cold-worked layer and the surface topography should be considered together when discussing the effects of the surface state on the morphologies of the oxide films.
部门归属	[ming, h. -l. ; zhang, z. -m. ; wang, s. -y. ; wang, j. -q. ; han, e. -h. ; ke, w.] chinese acad sci, key lab nucl mat & safety assessment, inst met res, shenyang 110016, peoples r china
资助者	Special Funds for the Major State Basic Research Projects [G2011CB610502]; National Science and Technology Major Project [2011ZX06004-009]
收录类别	sci
语种	英语
WOS记录号	WOS:000360965400005
引用统计	被引频次：15[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/75114
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	Ming, H. -L.,Zhang, Z. -M.,Wang, S. -Y.,et al. Short time oxidation behavior of 308L weld metal and 316L stainless steel with different surface state in simulated primary water with 0.1 mg/L dissolved oxygen[J]. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,2015,66(9):869-881.
APA	Ming, H. -L.,Zhang, Z. -M.,Wang, S. -Y.,Wang, J. -Q.,Han, E. -H.,&Ke, W..(2015).Short time oxidation behavior of 308L weld metal and 316L stainless steel with different surface state in simulated primary water with 0.1 mg/L dissolved oxygen.MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,66(9),869-881.
MLA	Ming, H. -L.,et al."Short time oxidation behavior of 308L weld metal and 316L stainless steel with different surface state in simulated primary water with 0.1 mg/L dissolved oxygen".MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION 66.9(2015):869-881.