|The effect of dissolved oxygen on fatigue behavior of Alloy 690 steam generator tubes in borated and lithiated high temperature water|
|Tan, Jibo; Wu, Xinqiang; Han, En-Hou; Liu, Xiaoqiang; Xu, Xuelian; Sun, Haitao; email@example.com
|摘要||Corrosion fatigue behavior of Alloy 690 tubes used for actual steam generator (SG) was investigated in borated and lithiated high temperature water containing <5 ppb (by weight) and 5500 ppb dissolved oxygen (DO) using boat-shaped specimens. It was found that the fatigue life at 5500 ppb DO was longer than at <5 ppb DO. The surface cracks and fracture characteristics of the specimens after fatigue tests were carefully examined. The effects of DO concentration on fatigue crack initiation and propagation of Alloy 690 tubes in high temperature water are discussed. (C) 2015 Elsevier Ltd. All rights reserved.|
; wu, xinqiang
; han, en-hou] chinese acad sci, liaoning key lab safety & assessment tech nucl ma, inst met res, key lab nucl mat & safety assessment, shenyang 110016, peoples r china
; [liu, xiaoqiang
; xu, xuelian] shanghai nucl engn res & design inst, shanghai 200233, peoples r china
; [sun, haitao] sepa, nucl & radiat safety ctr, beijing 100082, peoples r china
High Temperature Corrosion
|资助者||Science and Technology Foundation of China ; Special Funds for the Major State Basic Research Projects [2011CB610506]; Science and Technology Project of Yunnan Province; Technology Development (Cooperation) Fund from Yunnan Wenshan Dounan Manganese Industry Co., Ltd.; Innovation Fund of Institute of Metal Research (IMR), Chinese Academy of Sciences (CAS)
Tan, Jibo,Wu, Xinqiang,Han, En-Hou,et al. The effect of dissolved oxygen on fatigue behavior of Alloy 690 steam generator tubes in borated and lithiated high temperature water[J]. CORROSION SCIENCE,2016,102:394-404.
Tan, Jibo.,Wu, Xinqiang.,Han, En-Hou.,Liu, Xiaoqiang.,Xu, Xuelian.,...&firstname.lastname@example.org.(2016).The effect of dissolved oxygen on fatigue behavior of Alloy 690 steam generator tubes in borated and lithiated high temperature water.CORROSION SCIENCE,102,394-404.
Tan, Jibo,et al."The effect of dissolved oxygen on fatigue behavior of Alloy 690 steam generator tubes in borated and lithiated high temperature water".CORROSION SCIENCE 102(2016):394-404.