The influence of the chemically bonded interface between fillers and binder on the failure behaviour of an epoxy coating under marine alternating hydrostatic pressure

IMR OpenIR

	The influence of the chemically bonded interface between fillers and binder on the failure behaviour of an epoxy coating under marine alternating hydrostatic pressure
	Meng, Fandi; Liu, Li; Tian, Wenliang; Wu, Hang; Li, Ying; Zhang, Tao; Wang, Fuhui; liliu@imr.ac.cn
	2015
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	101 页码:139-154
摘要	The failure behaviour of epoxy resin-based modified mica (MM) coating has been investigated under marine alternating hydrostatic pressure (AHP). The results indicate that the chemically bonded interface forms between MM fillers and epoxy binder, which significantly enhances the compactness and the mechanical properties of coating by promoting the dispersion of fillers and reducing the defects of coating. The improvement of the fillers/binder interface weakens the permeation of water and the deterioration of coating structure which are caused by the drawing force of AHP. Hence, the performance of epoxy coating is promoted under AHP environment. (C) 2015 Elsevier Ltd. All rights reserved.
部门归属	[meng, fandi ; liu, li ; tian, wenliang ; wu, hang ; li, ying ; zhang, tao ; wang, fuhui] chinese acad sci, inst met res, shenyang 110016, peoples r china ; [zhang, tao ; wang, fuhui] harbin engn univ, minist educ, key lab superlight mat & surface technol, corros & protect lab, harbin 150001, peoples r china
关键词	Organic Coatings Eis Sem Interfaces
资助者	National Basic Research Program of China; Ministry of Science and Technology China [2014CB643303]; National Natural Science Fund of China [51271187]
收录类别	sci
语种	英语
WOS记录号	WOS:000364271700014
引用统计	被引频次：134[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/75197
专题	中国科学院金属研究所
通讯作者	liliu@imr.ac.cn
推荐引用方式 GB/T 7714	Meng, Fandi,Liu, Li,Tian, Wenliang,et al. The influence of the chemically bonded interface between fillers and binder on the failure behaviour of an epoxy coating under marine alternating hydrostatic pressure[J]. CORROSION SCIENCE,2015,101:139-154.
APA	Meng, Fandi.,Liu, Li.,Tian, Wenliang.,Wu, Hang.,Li, Ying.,...&liliu@imr.ac.cn.(2015).The influence of the chemically bonded interface between fillers and binder on the failure behaviour of an epoxy coating under marine alternating hydrostatic pressure.CORROSION SCIENCE,101,139-154.
MLA	Meng, Fandi,et al."The influence of the chemically bonded interface between fillers and binder on the failure behaviour of an epoxy coating under marine alternating hydrostatic pressure".CORROSION SCIENCE 101(2015):139-154.