Thermal cycling, microstructure and mechanical properties of 9Cr2WVTa steel welds
Wang, Jian; Lu, Shanping; Rong, Lijian; Li, Dianzhong; shplu@imr.ac.cn
2015
Source PublicationJOURNAL OF MATERIALS PROCESSING TECHNOLOGY
ISSN0924-0136
Volume222Pages:434-443
AbstractSamples of enlarged heat affected zones (HAZs) submitted to single and double welding thermal cycles were fabricated by a thermal-mechanical physical simulator (Gleeble 1500). Typical welding thermal cycle curves were extracted based on the measurement of the non-equilibrium phase transformation of 9Cr2WVTa steel, and the simulated and experimental thermal cycles were compared. Observation of the microstructure revealed that the blocky delta-ferrite that existed in the coarse grained heat affected zone (CGHAZ) was the main cause of the decrease in impact toughness. Each of the areas retained the delta-ferrite with different sizes and shapes after the CGHAZ underwent the second welding thermal cycle. Hardness tests, tensile tests, and instrumented impact tests were carried out to investigate the corresponding mechanical properties. When the peak temperature of the second welding thermal cycle was 1315 degrees C, grain and structure coarsening was the main causes of the decrease in impact toughness. When the peak temperature of the second welding thermal cycle was decreased to 1100 degrees C, the toughness increased the most due to the fine grains formed by phase transformation recrystallization. (C) 2015 Elsevier B.V. All rights reserved.
description.department[wang, jian ; lu, shanping ; li, dianzhong] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china ; [wang, jian ; rong, lijian] chinese acad sci, inst met res, key lab nucl mat & safety assessment, shenyang 110016, peoples r china
Keyword9cr2wvta Steel Welding Thermal Cycle Delta Ferrite Grain And Structure Coarsening Phase Transformation Recrystallization
Funding OrganizationNational Natural Science Foundation of China [91226204]; Chinese Academy of Science Strategic Pilot Project [XDA03010304]
Indexed Bysci
Language英语
WOS IDWOS:000355029100046
Citation statistics
Cited Times:14[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/75214
Collection中国科学院金属研究所
Corresponding Authorshplu@imr.ac.cn
Recommended Citation
GB/T 7714
Wang, Jian,Lu, Shanping,Rong, Lijian,et al. Thermal cycling, microstructure and mechanical properties of 9Cr2WVTa steel welds[J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY,2015,222:434-443.
APA Wang, Jian,Lu, Shanping,Rong, Lijian,Li, Dianzhong,&shplu@imr.ac.cn.(2015).Thermal cycling, microstructure and mechanical properties of 9Cr2WVTa steel welds.JOURNAL OF MATERIALS PROCESSING TECHNOLOGY,222,434-443.
MLA Wang, Jian,et al."Thermal cycling, microstructure and mechanical properties of 9Cr2WVTa steel welds".JOURNAL OF MATERIALS PROCESSING TECHNOLOGY 222(2015):434-443.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Wang, Jian]'s Articles
[Lu, Shanping]'s Articles
[Rong, Lijian]'s Articles
Baidu academic
Similar articles in Baidu academic
[Wang, Jian]'s Articles
[Lu, Shanping]'s Articles
[Rong, Lijian]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Wang, Jian]'s Articles
[Lu, Shanping]'s Articles
[Rong, Lijian]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.