Wear behaviour of WC-Co HVOF coatings at different temperatures in air and argon
Geng, Z.; Li, S.; Duan, D. L.; Liu, Y.; duandl@imr.ac.cn
2015
发表期刊WEAR
ISSN0043-1648
卷号330页码:348-353
摘要The wear behaviour of tungsten carbide-cobalt (WC-Co) high-velocity oxy-fuel coatings within the range of room temperature (RT) to 800 degrees C in air and RT to 650 degrees C in argon was studied using a ball-on-disc tribometer. The worn track morphologies, compositions and oxide phases after the tests were analysed by scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction analysis and Raman spectroscopy. The correlation between the oxidation and wear of WC-Co coatings was investigated. Results show that oxides, as well as the oxidation of coatings, have an important role during the tribological process of WC-Co coatings. The volume loss of WC-Co coatings in air is low at RT to 600 degrees C, which indicates that oxidation inhibits wear. Friction promotes the formation of CoWO4. CoWO4 can reduce friction and wear, and enables the coating to maintain good tribological properties even at 600 degrees C. Above 600 degrees C, the coating oxidises vigorously and its property deteriorates rapidly, which cause serious wear. In argon, the volume loss of WC-Co coating is significantly higher than that in air at RT to 600 C. Wear decreases as temperature rises because of the gradual formation of oxides. Consequently, WC-Co coatings should not be used as wearresistant coatings in 0-deficient environments at RT or at elevated temperatures. (C) 2015 Elsevier B.V. All rights reserved.
部门归属[geng, z. ; li, s. ; duan, d. l. ; liu, y.] chinese acad sci, inst met res, shenyang 110016, liaoning, peoples r china ; [geng, z.] tsinghua univ, state key lab tribol, beijing 100084, peoples r china
关键词Thermally Sprayed Wc-co Coating Wear Oxide Temperature
收录类别sci
语种英语
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/75243
专题中国科学院金属研究所
通讯作者duandl@imr.ac.cn
推荐引用方式
GB/T 7714
Geng, Z.,Li, S.,Duan, D. L.,et al. Wear behaviour of WC-Co HVOF coatings at different temperatures in air and argon[J]. WEAR,2015,330:348-353.
APA Geng, Z.,Li, S.,Duan, D. L.,Liu, Y.,&duandl@imr.ac.cn.(2015).Wear behaviour of WC-Co HVOF coatings at different temperatures in air and argon.WEAR,330,348-353.
MLA Geng, Z.,et al."Wear behaviour of WC-Co HVOF coatings at different temperatures in air and argon".WEAR 330(2015):348-353.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Geng, Z.]的文章
[Li, S.]的文章
[Duan, D. L.]的文章
百度学术
百度学术中相似的文章
[Geng, Z.]的文章
[Li, S.]的文章
[Duan, D. L.]的文章
必应学术
必应学术中相似的文章
[Geng, Z.]的文章
[Li, S.]的文章
[Duan, D. L.]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。