EIS analysis on stress corrosion initiation of pipeline steel under disbonded coating in near-neutral pH simulated soil electrolyte

IMR OpenIR

	EIS analysis on stress corrosion initiation of pipeline steel under disbonded coating in near-neutral pH simulated soil electrolyte
	Maocheng, Y. A. N.; Jin, X. U.; Libao, Y. U.; Tangqing, W. U.; Cheng, S. U. N.; Wei, K. E.; Maocheng, YAN (reprint author), Chinese Acad Sci, Environm Corros Ctr, Inst Met Res, Shenyang 110016, Peoples R China.
	2016-09-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	110 页码:23-34
摘要	Initiation of stress corrosion of X80 high strength low alloy (HSLA) pipeline steel in a near-neutral pH environment was investigated in a crevice cell simulating coating disbondment. Multi specimens were loaded simultaneously by a loading frame. EIS was applied to characterize behavior of SCC and local electrochemical process. Results indicate that the steel under disbonded coating is in an active dissolution state. In-depth profile of the reciprocal charge transfer resistance shows a decreasing trend over distance from the opening. A shielding factor was proposed to characterize shielding effect of disbondment on stress corrosion of pipeline steels. (C) 2016 Elsevier Ltd. All rights reserved.
部门归属	[maocheng, y. a. n. ; jin, x. u. ; libao, y. u. ; tangqing, w. u. ; cheng, s. u. n. ; wei, k. e.] chinese acad sci, environm corros ctr, inst met res, shenyang 110016, peoples r china
关键词	Carbon Steel Stress Corrosion Eis Sem Crevice Corrosion
学科领域	Materials Science ; Metallurgy & Metallurgical Engineering
资助者	National Science Foundation of China [51131001, 51471176]; Natural Science Foundation of Liaoning Province [2015020174]; National RD Infrastructure and Facility Development Program of China [2005DKA10400CT-2-02]
收录类别	sci
语种	英语
WOS记录号	WOS:000379564500003
引用统计	被引频次：96[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/75761
专题	中国科学院金属研究所
通讯作者	Maocheng, YAN (reprint author), Chinese Acad Sci, Environm Corros Ctr, Inst Met Res, Shenyang 110016, Peoples R China.
推荐引用方式 GB/T 7714	Maocheng, Y. A. N.,Jin, X. U.,Libao, Y. U.,et al. EIS analysis on stress corrosion initiation of pipeline steel under disbonded coating in near-neutral pH simulated soil electrolyte[J]. CORROSION SCIENCE,2016,110:23-34.
APA	Maocheng, Y. A. N..,Jin, X. U..,Libao, Y. U..,Tangqing, W. U..,Cheng, S. U. N..,...&Maocheng, YAN .(2016).EIS analysis on stress corrosion initiation of pipeline steel under disbonded coating in near-neutral pH simulated soil electrolyte.CORROSION SCIENCE,110,23-34.
MLA	Maocheng, Y. A. N.,et al."EIS analysis on stress corrosion initiation of pipeline steel under disbonded coating in near-neutral pH simulated soil electrolyte".CORROSION SCIENCE 110(2016):23-34.