|Influence of substrate composition on the oxidation performance of nickel aluminide coating prepared by pack cementation|
|Zhou, Yuhua; Wang, Li; Wang, Guan; Jin, Dongliang; Hao, Wei; Zhao, Xiaofeng; Zhang, Jian; Xiao, Ping; Zhao, XF (reprint author), Shanghai Jiao Tong Univ, Shanghai Key Lab High Temp Mat & Precis Forming, Shanghai 200240, Peoples R China.
|摘要||Effects of substrate compositions on the microstructure and oxidation behavior of NiAl coating by pack cementation were investigated. It is found that substrate compositions have a profound influence on the coating microstructure and oxidation performance. The DZ125 and DD6 coating systems exhibit better spallation resistance due to the presence of Hf. The interface rumpling, as well as the TiO2 and Ti-rich oxide are responsible for the oxide spallation of the DZ411 coating system. The voids at the oxide/coating interface, leading to a lower interfacial adhesion, result in the worst oxide spallation of the Ni and Hastelloy X coating systems. (C) 2016 Elsevier Ltd. All rights reserved.|
; wang, guan
; jin, dongliang
; hao, wei
; zhao, xiaofeng
; xiao, ping] shanghai jiao tong univ, shanghai key lab high temp mat & precis forming, shanghai 200240, peoples r china
; [wang, li
; zhang, jian] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china
; [xiao, ping] univ manchester, sch mat, grosvenor st, manchester m1 7hs, lancs, england
; Metallurgy & Metallurgical Engineering
|资助者||Qianren Plan Platform Funding; Program for Professor of Special Appointment (Eastern Scholar) at Shanghai Institutions of Higher Learning [SHDP201303]; National Natural Science Foundation of China 
|通讯作者||Zhao, XF (reprint author), Shanghai Jiao Tong Univ, Shanghai Key Lab High Temp Mat & Precis Forming, Shanghai 200240, Peoples R China.|
Zhou, Yuhua,Wang, Li,Wang, Guan,et al. Influence of substrate composition on the oxidation performance of nickel aluminide coating prepared by pack cementation[J]. CORROSION SCIENCE,2016,110:284-295.
Zhou, Yuhua.,Wang, Li.,Wang, Guan.,Jin, Dongliang.,Hao, Wei.,...&Zhao, XF .(2016).Influence of substrate composition on the oxidation performance of nickel aluminide coating prepared by pack cementation.CORROSION SCIENCE,110,284-295.
Zhou, Yuhua,et al."Influence of substrate composition on the oxidation performance of nickel aluminide coating prepared by pack cementation".CORROSION SCIENCE 110(2016):284-295.