Investigation into the failure mechanism of chromia scale thermally grown on an austenitic stainless steel in pure steam

IMR OpenIR

	Investigation into the failure mechanism of chromia scale thermally grown on an austenitic stainless steel in pure steam
	Yuan, Juntao; Wang, Wen; Zhang, Huihui; Zhu, Lijuan; Zhu, Shenglong; Wang, Fuhui; Yuan, JT (reprint author), CNPC, State Key Lab & Struct Safety Petr Tubular Goods, Tubular Goods Res Inst, Xian 710077, Peoples R China.
	2016-08-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	109 页码:36-42
摘要	The corrosion behavior of a commercial austenitic stainless steel HR3C was investigated in air and in pure steam at 700 degrees C, and the results are compared. The results show that the chromium concentration in HR3C was sufficient to form protective chromia scale initially in both environments. The oxide scales thermally grown in pure steam, however, were apt to lose their protectiveness by cracking and buckling. A failure mechanism of chromia scale thermally grown in pure steam is proposed by considering influences of hydrogen produced during steam oxidation in terms of molecular hydrogen and hydrogen defects. (C) 2016 Elsevier Ltd. All rights reserved.
部门归属	[yuan, juntao ; zhu, lijuan] cnpc, state key lab performance & struct safety petr tu, tubular goods res inst, xian 710077, peoples r china ; [yuan, juntao ; wang, wen ; zhang, huihui ; zhu, lijuan ; zhu, shenglong ; wang, fuhui] chinese acad sci, inst met res, key lab corros & protect, shenyang 110016, peoples r china ; [zhang, huihui] xian univ sci & technol, coll mat sci & engn, xian 710054, peoples r china
关键词	Stainless Steel Sem Xrd Xps High Temperature Corrosion
学科领域	Materials Science ; Metallurgy & Metallurgical Engineering
资助者	National Nature Science Foundation of China [51071163, 51301202]; National Key Basic Research Program of China (973 Program) [2012CB625102]; Education Department of Shaanxi Provincial Government [15JK1489]
收录类别	sci
语种	英语
WOS记录号	WOS:000377232100004
引用统计	被引频次：38[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/75780
专题	中国科学院金属研究所
通讯作者	Yuan, JT (reprint author), CNPC, State Key Lab & Struct Safety Petr Tubular Goods, Tubular Goods Res Inst, Xian 710077, Peoples R China.
推荐引用方式 GB/T 7714	Yuan, Juntao,Wang, Wen,Zhang, Huihui,et al. Investigation into the failure mechanism of chromia scale thermally grown on an austenitic stainless steel in pure steam[J]. CORROSION SCIENCE,2016,109:36-42.
APA	Yuan, Juntao.,Wang, Wen.,Zhang, Huihui.,Zhu, Lijuan.,Zhu, Shenglong.,...&Yuan, JT .(2016).Investigation into the failure mechanism of chromia scale thermally grown on an austenitic stainless steel in pure steam.CORROSION SCIENCE,109,36-42.
MLA	Yuan, Juntao,et al."Investigation into the failure mechanism of chromia scale thermally grown on an austenitic stainless steel in pure steam".CORROSION SCIENCE 109(2016):36-42.