The Minor Precipitation at the Final Stage of U720Li Solidification
Zhao, Guang-Di; Yu, Lian-Xu; Qi, Feng; Liu, Fang; Sun, Wen-Ru; Hu, Zhuang-Qi; Sun, WR (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China.
2016-06-01
Source PublicationACTA METALLURGICA SINICA-ENGLISH LETTERS
ISSN1006-7191
Volume29Issue:6Pages:518-526
AbstractThe minor precipitations caused by B and Zr which are the normal constituents of U720Li alloy have been studied by analyzing the solidification process and the composition evolution. The present study aims to supply the elementary information about the existing form of B and Zr in the as-cast microstructure, which is helpful for the subsequent processing, such as homogenization treatment. The M3B2 and Ni5Zr phases were observed in the U720Li alloy in as-cast state, which were usually accompanying with each other together with eta-Ni3Ti phase at the edge of eutectic (gamma + gamma'). Combining the DTA analysis and heating and quenching tests, the solidification sequence was determined to be the following: gamma matrix, eutectic (gamma + gamma'), eta-Ni3Ti, M3B2 and Ni5Zr. The in situ composition analysis by EDS and EPMA revealed that the precipitation and microstructure were governed by the composition evolution in the liquids. The solidification of gamma matrix increased the Ti concentration in the residual liquids and resulted in the eutectic (gamma + gamma') formation; the (gamma + gamma') formation increased the Ti/Al radio in the liquids and the eta-Ni3Ti was formed in front of the eutectic (gamma + gamma'); the eta-Ni3Ti precipitation consumed up Al and Ti and increased the concentration of B, Mo and Cr, and M3B2 boride is formed; the previous precipitation of the phases consumed up most of the elements other than Ni and Zr, and Ni5Zr is formed finally. The melting points are in the ranges of 1130-1140 degrees C for Ni5Zr phase, 1180-1190 degrees C for M3B2 boride and 1190-1200 degrees C for eta-Ni3Ti phase.
description.department[zhao, guang-di ; yu, lian-xu ; qi, feng ; liu, fang ; sun, wen-ru ; hu, zhuang-qi] chinese acad sci, inst met res, shenyang 110016, peoples r china ; [zhao, guang-di] univ sci & technol china, sch mat sci & engn, hefei 230026, peoples r china
KeywordSuperalloy U720li Solidification M3b2 Boride Ni5zr Phase
Subject AreaMetallurgy & Metallurgical Engineering
Indexed Bysci
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/75848
Collection中国科学院金属研究所
Corresponding AuthorSun, WR (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China.
Recommended Citation
GB/T 7714
Zhao, Guang-Di,Yu, Lian-Xu,Qi, Feng,et al. The Minor Precipitation at the Final Stage of U720Li Solidification[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2016,29(6):518-526.
APA Zhao, Guang-Di.,Yu, Lian-Xu.,Qi, Feng.,Liu, Fang.,Sun, Wen-Ru.,...&Sun, WR .(2016).The Minor Precipitation at the Final Stage of U720Li Solidification.ACTA METALLURGICA SINICA-ENGLISH LETTERS,29(6),518-526.
MLA Zhao, Guang-Di,et al."The Minor Precipitation at the Final Stage of U720Li Solidification".ACTA METALLURGICA SINICA-ENGLISH LETTERS 29.6(2016):518-526.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhao, Guang-Di]'s Articles
[Yu, Lian-Xu]'s Articles
[Qi, Feng]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhao, Guang-Di]'s Articles
[Yu, Lian-Xu]'s Articles
[Qi, Feng]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhao, Guang-Di]'s Articles
[Yu, Lian-Xu]'s Articles
[Qi, Feng]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.