Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water

IMR OpenIR

	Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water
	Dong, Lijin; Peng, Qunjia; Han, En-Hou; Ke, Wei; Wang, Lei; Peng, QJ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China.
	2016-06-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	107 页码:172-181
摘要	Stress corrosion cracking (SCC) in the heat affected zone (HAZ) of a stainless steel 308L-316L weld joint in primary water of pressurized water reactor was investigated. Stress corrosion crack growth in the HAZ was observed in off-normal primary water chemistry with dissolved oxygen, but not in normal primary water chemistry with dissolved hydrogen. This suggests that it is unlikely a stress corrosion crack propagating in the HAZ could reach the fusion boundary and penetrate into the weld metal under normal primary water chemistry conditions. Microstructure analysis of the crack tip suggests that the SCC follows the slip-oxidation mechanism. (C) 2016 Elsevier Ltd. All rights reserved.
部门归属	[dong, lijin ; peng, qunjia ; han, en-hou ; ke, wei] chinese acad sci, inst met res, key lab nucl mat & safety assessment, shenyang 110016, peoples r china ; [dong, lijin ; wang, lei] northeastern univ, key lab anisotropy & texture mat, minist educ, shenyang 110819, peoples r china
关键词	Stainless Steel Sem Tem Stress Corrosion Welding
学科领域	Materials Science ; Metallurgy & Metallurgical Engineering
资助者	Hundred-Talent program of Chinese Academy of Sciences; National Natural Science Foundation of China [51571204]
收录类别	sci
语种	英语
WOS记录号	WOS:000374358900017
引用统计	被引频次：66[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/75863
专题	中国科学院金属研究所
通讯作者	Peng, QJ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China.
推荐引用方式 GB/T 7714	Dong, Lijin,Peng, Qunjia,Han, En-Hou,et al. Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water[J]. CORROSION SCIENCE,2016,107:172-181.
APA	Dong, Lijin,Peng, Qunjia,Han, En-Hou,Ke, Wei,Wang, Lei,&Peng, QJ .(2016).Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water.CORROSION SCIENCE,107,172-181.
MLA	Dong, Lijin,et al."Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water".CORROSION SCIENCE 107(2016):172-181.