Effect of carbon content on microstructures, mechanical and tribological properties and thermal stability in WBC films

IMR OpenIR

	Effect of carbon content on microstructures, mechanical and tribological properties and thermal stability in WBC films
	Liu, Y. M.; Pei, Z. L.; Gong, J.; Sun, C.; Pei, ZL (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China.
	2016-04-15
发表期刊	SURFACE & COATINGS TECHNOLOGY
ISSN	0257-8972
卷号	271 页码:276-285
摘要	The study is mainly to develop a new type of hard nanocomposite films based on the AlB2-type WB2 (h-WB2) system by studying the influence of carbon contents on the microstructures, mechanical and tribological properties, and thermal stability of the WBC films. By increasing the C2H2 partial pressure (P-C2H2), carbon atoms present in forms of solid solution h-WBxCy and amorphous carbide a-WC, a-WBxCy, a-C:H (polymeric carbon) successively. Consequently, two- or three-phase nanocomposite films with microstructures comprising of nanocrystalline grains embedded in an amorphous matrix have been developed. Films with the h-WBxCy/a-WC and h-WBxCy/a-WC/a-C:H (or h-WBxCy/a-WBxCy/a-WC/a-C:H) nanocomposite structure deposited at P-C2H2 <= 0.01 Pa (14.9-26.4 at.% C) exhibit highest hardness about 45 GPa and lowest wear rate about 10(-8) mm(3)/mN. And the transformation temperature of the h-WB2 phase has been enhanced greatly from 700 to 1000 degrees C by slight C-doping due to the formation of the strong interfaces between the nanocrystalline and amorphous phase in the films deposited at P-C2H2 = 0.008 Pa. Moreover, proper C content (less than 26.4 at.%) can refine the film structure and reduce the oxygen impurity content and thereby improve the film properties. The residual stress of the films changes from tensile to compressive stress with the introduction of carbon, and the value of compressive stress is closely related to the film structures. (C) 2016 Elsevier B.V. All rights reserved.
部门归属	[liu, y. m.] xian shiyou univ, coll mat sci & engn, xian 710065, peoples r china ; [liu, y. m. ; pei, z. l. ; gong, j. ; sun, c.] chinese acad sci, inst met res, shenyang 110016, peoples r china
关键词	Reactive Magnetron Sputtering Nanocomposites Wbc Films Mechanical Properties Tribological Properties Thermal Stability
学科领域	Materials Science ; Physics
资助者	National Key Basic Research Program of China (973 Program) [2012CB625100]; Natural Science Foundation of Liaoning Province of China [2013020093]
收录类别	sci
语种	英语
WOS记录号	WOS:000374609900031
引用统计
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/75907
专题	中国科学院金属研究所
通讯作者	Pei, ZL (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China.
推荐引用方式 GB/T 7714	Liu, Y. M.,Pei, Z. L.,Gong, J.,et al. Effect of carbon content on microstructures, mechanical and tribological properties and thermal stability in WBC films[J]. SURFACE & COATINGS TECHNOLOGY,2016,271:276-285.
APA	Liu, Y. M.,Pei, Z. L.,Gong, J.,Sun, C.,&Pei, ZL .(2016).Effect of carbon content on microstructures, mechanical and tribological properties and thermal stability in WBC films.SURFACE & COATINGS TECHNOLOGY,271,276-285.
MLA	Liu, Y. M.,et al."Effect of carbon content on microstructures, mechanical and tribological properties and thermal stability in WBC films".SURFACE & COATINGS TECHNOLOGY 271(2016):276-285.