|Corrosion Behavior of Pure Ti under a Solid NaCl Deposit in a Wet Oxygen Flow at 600 degrees C|
|Fan, Lei; Liu, Li; Cao, Min; Yu, Zhongfen; Li, Ying; Chen, Minghui; Wang, Fuhui; Liu, L; Li, Y (reprint author), Chinese Acad Sci, Inst Met Res, Wencui Rd 62, Shenyang 110016, Peoples R China.
|摘要||The corrosion behavior of pure Ti under a solid NaCl deposit in a wet O-2 flow at 600 degrees C has been studied. The results showed that the corrosion rate was greatly accelerated by solid NaCl, which destroyed the compact and protective TiO2 scale to yield non-protective N4Ti5O12 and other products. Detailed scanning electron microscopy (SEM) equipped with an energy dispersive spectrometer (EDX), and X-ray diffraction (XRD) analysis showed that, during the corrosion process, the metal (Ti) diffused outward rapidly and reacted with the wet O-2 to form a thick and porous corrosion products scale. The electrochemical reaction was also observed during the whole corrosion process at 600 degrees C, which further accelerated the corrosion rate. A possible mechanism has been proposed for pure Ti covered with a solid NaCl deposit in wet O-2 at 600 degrees C, based on the experimental results.|
; liu, li
; cao, min
; li, ying
; wang, fuhui] chinese acad sci, inst met res, wencui rd 62, shenyang 110016, peoples r china
; [yu, zhongfen
; chen, minghui
; wang, fuhui] northeastern univ, sch mat sci & engn, key lab anisotropy & texture mat moe, shenyang 110819, peoples r china
Solid Nacl Deposit
; Metallurgy & Metallurgical Engineering
|资助者||National Key Basic Research and Development Plan of China [2014CB643303]; National Natural Science Foundation of China [51371181, 51531007]; International S&T Cooperation Program of China (ISTCP) [2014DFR50560]
|通讯作者||Liu, L; Li, Y (reprint author), Chinese Acad Sci, Inst Met Res, Wencui Rd 62, Shenyang 110016, Peoples R China.|
Fan, Lei,Liu, Li,Cao, Min,et al. Corrosion Behavior of Pure Ti under a Solid NaCl Deposit in a Wet Oxygen Flow at 600 degrees C[J]. METALS,2016,6(4).
Fan, Lei.,Liu, Li.,Cao, Min.,Yu, Zhongfen.,Li, Ying.,...&Li, Y .(2016).Corrosion Behavior of Pure Ti under a Solid NaCl Deposit in a Wet Oxygen Flow at 600 degrees C.METALS,6(4).
Fan, Lei,et al."Corrosion Behavior of Pure Ti under a Solid NaCl Deposit in a Wet Oxygen Flow at 600 degrees C".METALS 6.4(2016).