Corrosion resistance of self-growing TiC coating on SIMP steel in LBE at 600 degrees C
Shi, QQ; Yan, W; Sha, W; Wang, W; Shan, YY; Yang, K; Yan, W (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China.
2016-11-01
Source PublicationMATERIALS AND CORROSION-WERKSTOFFE UND KORROSION
ISSN0947-5117
Volume67Issue:11Pages:1204-1212
AbstractSIMP steel was newly developed as a candidate structural material for the accelerator driven subcritical system. The serious decarburization of SIMP steel because of the high Si content was used to successfully form a self-growing TiC coating on the surface, after the Ti deposition as a first step. This TiC layer can effectively protect the surface from the static liquid lead-bismuth eutectic (LBE) corrosion at 600 degrees C up to 2000h in the low oxygen LBE. However, in the oxygen saturated LBE, the TiC coating is oxidized into porous TiO2 after only 500h and fails to protect. Therefore, the self-growing TiC coating is desired only when the oxygen content of LBE is strictly controlled on a low level.
description.department[shi, q. -q. ; yan, w. ; wang, w. ; shan, y. -y. ; yang, k.] chinese acad sci, inst met res, key lab nucl mat & safety assessment, shenyang 110016, peoples r china ; [sha, w.] queens univ belfast, sch nat & built environm, belfast bt9 5ag, antrim, north ireland
KeywordLbe Self-growing Simp Steel Tic Coating
Subject AreaMaterials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
Funding OrganizationAdvanced Fission Energy Program-ADS Transmutation System, Chinese Academy of Sciences [XDA03010301, XDA03010302, XDA03010000]
Indexed Bysci
Language英语
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/76198
Collection中国科学院金属研究所
Corresponding AuthorYan, W (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China.
Recommended Citation
GB/T 7714
Shi, QQ,Yan, W,Sha, W,et al. Corrosion resistance of self-growing TiC coating on SIMP steel in LBE at 600 degrees C[J]. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,2016,67(11):1204-1212.
APA Shi, QQ.,Yan, W.,Sha, W.,Wang, W.,Shan, YY.,...&Yan, W .(2016).Corrosion resistance of self-growing TiC coating on SIMP steel in LBE at 600 degrees C.MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,67(11),1204-1212.
MLA Shi, QQ,et al."Corrosion resistance of self-growing TiC coating on SIMP steel in LBE at 600 degrees C".MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION 67.11(2016):1204-1212.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Shi, QQ]'s Articles
[Yan, W]'s Articles
[Sha, W]'s Articles
Baidu academic
Similar articles in Baidu academic
[Shi, QQ]'s Articles
[Yan, W]'s Articles
[Sha, W]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Shi, QQ]'s Articles
[Yan, W]'s Articles
[Sha, W]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.