Stress corrosion cracking of 316L HAZ for 316L stainless steel/Inconel 52M dissimilar metal weld joint in simulated primary water
Zhu, RL; Wang, JQ; Zhang, LT; Zhang, ZM; Han, EH; Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China.
2016-11-01
发表期刊CORROSION SCIENCE
ISSN0010-938X
卷号112页码:373-384
摘要The stress corrosion cracking (SCC) behaviour of 316L heat affected zones (HAZ) in 316L stainless steel/Inconel 52M dissimilar metal welded joint (DMWJ) in simulated primary water was systematically evaluated using direct current potential drop (DCPD) methods. Crack growth rates (CGRs) of 316L HAZ increased with increasing temperature and dissolved oxygen (DO) contents. CGR in hydrogenated water was approximately one order of magnitude slower than in oxygenated water. The fracture surface shows typical mixed intergranular-transgranular SCC characteristics and several fast finger-like cracks. Several intergranular secondary cracks, perpendicular to the main crack and fusion boundary, were also observed. (C) 2016 Elsevier Ltd. All rights reserved.
部门归属[zhu, ruolin ; wang, jianqiu ; zhang, litao ; zhang, zhiming ; han, en-hou] chinese acad sci, inst met res, key lab nucl mat & safety assessment, shenyang 110016, peoples r china ; [zhu, ruolin] univ chinese acad sci, 19 yuquan rd, beijing 100049, peoples r china
关键词Stainless Steel Nickel Sem Welding Stress Corrosion
学科领域Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
资助者Science and Technology Commission of Shanghai Municipality, Shanghai, PR China [14DZ2250300]
收录类别sci
语种英语
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/76213
专题中国科学院金属研究所
通讯作者Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China.
推荐引用方式
GB/T 7714
Zhu, RL,Wang, JQ,Zhang, LT,et al. Stress corrosion cracking of 316L HAZ for 316L stainless steel/Inconel 52M dissimilar metal weld joint in simulated primary water[J]. CORROSION SCIENCE,2016,112:373-384.
APA Zhu, RL,Wang, JQ,Zhang, LT,Zhang, ZM,Han, EH,&Wang, JQ .(2016).Stress corrosion cracking of 316L HAZ for 316L stainless steel/Inconel 52M dissimilar metal weld joint in simulated primary water.CORROSION SCIENCE,112,373-384.
MLA Zhu, RL,et al."Stress corrosion cracking of 316L HAZ for 316L stainless steel/Inconel 52M dissimilar metal weld joint in simulated primary water".CORROSION SCIENCE 112(2016):373-384.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Zhu, RL]的文章
[Wang, JQ]的文章
[Zhang, LT]的文章
百度学术
百度学术中相似的文章
[Zhu, RL]的文章
[Wang, JQ]的文章
[Zhang, LT]的文章
必应学术
必应学术中相似的文章
[Zhu, RL]的文章
[Wang, JQ]的文章
[Zhang, LT]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。