Enhanced Enhanced bonding property of cold-sprayed Zn-Al coating on interstitial-free steel substrate with a nanostructured surface layer
Liang, YL; Wang, ZB; Zhang, J; Zhang, JB; Lu, K; Wang, ZB (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Peoples R China.
2016-11-01
发表期刊APPLIED SURFACE SCIENCE
ISSN0169-4332
卷号385页码:341-348
摘要By means of surface mechanical attrition treatment (SMAT), a gradient nanostructured surface layer was fabricated on a hot-rolled interstitial-free steel plate. A Zn-Al coating was subsequently deposited on the SMAT sample by using cold spray process. The bonding property of the coating on the SMAT substrate was compared with that on the coarse-grained (CG) sample. Stud-pull tests showed that the bonding strength in the as-sprayed SMAT sample is 30% higher than that in the as-sprayed CG sample. No further improvement in bonding strength was achieved in the coated SMAT sample after annealing at 400 degrees C, mostly due to the formation of cracks and intermetallic compounds at the coating/substrate interface in an earlier stage (<30 min) and in a final stage (>90 min), respectively. The enhanced bonding property of the Zn-Al coating on the SMAT sample might be related with the promoted atomic diffusion and hardness in the nanostructured surface layer. (C) 2016 Elsevier B.V. All rights reserved.
部门归属[liang, y. l.] univ sci & technol china, 96 jinzhai rd, hefei 230026, peoples r china ; [liang, y. l. ; wang, z. b. ; zhang, j. ; lu, k.] chinese acad sci, inst met res, shenyang natl lab mat sci, 72 wenhua rd, shenyang 110016, peoples r china ; [liang, y. l. ; zhang, j. b.] baoshan iron & steel co ltd, res inst, adv div technol, 655 fujin rd, shanghai 201900, peoples r china
关键词Nanostructured Surface Mechanical Attrition Treatment Cold Spray Interstitial-free Steel Bonding Strength
学科领域Chemistry, Physical ; Materials Science, Coatings & Films ; Physics, Applied ; Physics, Condensed Matter
资助者Ministry of Science and Technology projects of China [2012CB932203]; National Natural Science Foundation of China [51231006]; Key Research Program of Chinese Academy of Sciences [KGZD-EW-T06]; Shenyang National Laboratory for Materials Science
收录类别sci
语种英语
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/76227
专题中国科学院金属研究所
通讯作者Wang, ZB (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Peoples R China.
推荐引用方式
GB/T 7714
Liang, YL,Wang, ZB,Zhang, J,et al. Enhanced Enhanced bonding property of cold-sprayed Zn-Al coating on interstitial-free steel substrate with a nanostructured surface layer[J]. APPLIED SURFACE SCIENCE,2016,385:341-348.
APA Liang, YL,Wang, ZB,Zhang, J,Zhang, JB,Lu, K,&Wang, ZB .(2016).Enhanced Enhanced bonding property of cold-sprayed Zn-Al coating on interstitial-free steel substrate with a nanostructured surface layer.APPLIED SURFACE SCIENCE,385,341-348.
MLA Liang, YL,et al."Enhanced Enhanced bonding property of cold-sprayed Zn-Al coating on interstitial-free steel substrate with a nanostructured surface layer".APPLIED SURFACE SCIENCE 385(2016):341-348.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Liang, YL]的文章
[Wang, ZB]的文章
[Zhang, J]的文章
百度学术
百度学术中相似的文章
[Liang, YL]的文章
[Wang, ZB]的文章
[Zhang, J]的文章
必应学术
必应学术中相似的文章
[Liang, YL]的文章
[Wang, ZB]的文章
[Zhang, J]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。