Microstructure, Residual Strain and Stress Behavior in 316L Heat-Affected Zone
Ming, HL; Zhang, ZM; Xiu, PY; Wang, JQ; Han, EH; Ke, W; Su, MX; Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, Shenyang 110016, Peoples R China.
2016-09-01
发表期刊ACTA METALLURGICA SINICA-ENGLISH LETTERS
ISSN1006-7191
卷号29期号:9页码:848-858
摘要Austenitic stainless steels are usually chosen to make many components of nuclear power plants (NPPs). However, their microstructure in the heat-affected zone (HAZ) will change during the welding process. Some failures of the weld joints, mainly stress corrosion cracking (SCC), have been found to be located in the HAZ. In this research, the microstructure, micro-hardness, residual strain and SCC behavior at different locations of the 316L HAZ cut from a safe end dissimilar metal weld joint were studied. However, traditional optical microscope observation could not find any microstructural difference between the HAZ and the base metal, higher residual strain and micro-hardness, and higher fraction of random high-angle grain boundaries were found in the HAZ than in the base metal when studied by using electron back-scattering diffraction scanning and micro-hardness test. What's more, the residual strain, the micro-hardness and the fraction of random grain boundaries decreased, while the fraction of coincidence site lattice grain boundaries increased with increasing the distance from the fusion boundary in 316L HAZ. Creviced bent beam test was applied to evaluate the SCC susceptibility at different locations of 316L HAZ and base metal. It was found that the HAZ had higher SCC susceptibility than the base metal and SCC resistance increased when increasing the distance from the fusion boundary in 316L HAZ.
部门归属[ming, hong-liang ; zhang, zhi-ming ; xiu, peng-yuan ; wang, jian-qiu ; han, en-hou ; ke, wei] chinese acad sci, inst met res, key lab nucl mat & safety assessment, liaoning key lab safety & assessment tech nucl ma, shenyang 110016, peoples r china ; [ming, hong-liang] univ chinese acad sci, beijing 100049, peoples r china ; [su, ming-xing] shanghai res ctr weld & detect engn tech nucl equ, shanghai 201306, peoples r china
关键词Austenitic Stainless Steels Heat-affected Zone Microstructure Ebsd Residual Strain Stress Corrosion Cracking
学科领域Metallurgy & Metallurgical Engineering
资助者National Natural Science Foundation of China [51301183]; Science and Technology Commission of Shanghai Municipality, Shanghai, China [14DZ2250300]
收录类别sci
语种英语
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/76276
专题中国科学院金属研究所
通讯作者Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, Shenyang 110016, Peoples R China.
推荐引用方式
GB/T 7714
Ming, HL,Zhang, ZM,Xiu, PY,et al. Microstructure, Residual Strain and Stress Behavior in 316L Heat-Affected Zone[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2016,29(9):848-858.
APA Ming, HL.,Zhang, ZM.,Xiu, PY.,Wang, JQ.,Han, EH.,...&Wang, JQ .(2016).Microstructure, Residual Strain and Stress Behavior in 316L Heat-Affected Zone.ACTA METALLURGICA SINICA-ENGLISH LETTERS,29(9),848-858.
MLA Ming, HL,et al."Microstructure, Residual Strain and Stress Behavior in 316L Heat-Affected Zone".ACTA METALLURGICA SINICA-ENGLISH LETTERS 29.9(2016):848-858.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Ming, HL]的文章
[Zhang, ZM]的文章
[Xiu, PY]的文章
百度学术
百度学术中相似的文章
[Ming, HL]的文章
[Zhang, ZM]的文章
[Xiu, PY]的文章
必应学术
必应学术中相似的文章
[Ming, HL]的文章
[Zhang, ZM]的文章
[Xiu, PY]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。