Fatigue and Fracture Behavior of a Cold-Drawn Commercially Pure Aluminum Wire

IMR OpenIR

	Fatigue and Fracture Behavior of a Cold-Drawn Commercially Pure Aluminum Wire
	Hou, JP; Wang, Q; Yang, HJ; Wu, XM; Li, CH; Zhang, ZF; Li, XW; Li, XW (reprint author), Northeastern Univ, Sch Mat Sci & Engn, Dept Mat Phys & Chem, Shenyang 110819, Peoples R China.
	2016-09-01
发表期刊	MATERIALS
ISSN	1996-1944
卷号	9 期号:9
摘要	Fatigue properties and cracking behavior of cold-drawn commercially pure aluminum wires (CPAWs) widely used as the overhead transmission conductors were investigated. It was found that the fracture surface of the CPAWs shows an obvious four-stage fracture characteristic, i.e., crack initiation, planar crack propagation, 45 degrees-inclined crack propagation and final rapid fracture. The crack growth mechanisms for the CPAWs were found quite different from those for the conventional coarse-grained materials. The cracks in the CPAWs firstly grow along the grain boundaries (Stage I crack growth), and then grow along the plane of maximum shear stress during the last stage of cycling (Stage II crack growth), leading to the distinctive fracture surfaces, i.e., the granular surface in the planar crack propagation region and the coarse fatigue striations in the 45 degrees-inclined crack propagation region. The grain boundary migration was observed in the fatigued CPAWs. The increase in fatigue load enhances the dislocation recovery, increases the grain boundary migration rate, and thus promotes the occurrence of softening and damage localization up to the final failure.
部门归属	[hou, jia-peng ; li, xiao-wu] northeastern univ, sch mat sci & engn, dept mat phys & chem, shenyang 110819, peoples r china ; [hou, jia-peng ; wang, qiang ; yang, hua-jie ; zhang, zhe-feng] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china ; [wu, xi-mao ; li, chun-he] liaoning elect power co ltd, elect power res inst, shenyang 110006, peoples r china
关键词	Commercially Pure Aluminum Conductor Cold Drawing Tension-tension Fatigue Grain Boundary Migration Fracture
学科领域	Materials Science, Multidisciplinary
资助者	National Natural Science Foundation of China (NSFC) [51331007, 51271054, 51231002, 51571058]; Liaoning Electric Power Company Ltd.
收录类别	sci
语种	英语
WOS记录号	WOS:000384668700013
引用统计	被引频次：12[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/76283
专题	中国科学院金属研究所
通讯作者	Li, XW (reprint author), Northeastern Univ, Sch Mat Sci & Engn, Dept Mat Phys & Chem, Shenyang 110819, Peoples R China.
推荐引用方式 GB/T 7714	Hou, JP,Wang, Q,Yang, HJ,et al. Fatigue and Fracture Behavior of a Cold-Drawn Commercially Pure Aluminum Wire[J]. MATERIALS,2016,9(9).
APA	Hou, JP.,Wang, Q.,Yang, HJ.,Wu, XM.,Li, CH.,...&Li, XW .(2016).Fatigue and Fracture Behavior of a Cold-Drawn Commercially Pure Aluminum Wire.MATERIALS,9(9).
MLA	Hou, JP,et al."Fatigue and Fracture Behavior of a Cold-Drawn Commercially Pure Aluminum Wire".MATERIALS 9.9(2016).