Enhanced mechanical properties of medium carbon steel casting via friction stir processing and subsequent annealing

IMR OpenIR

	Enhanced mechanical properties of medium carbon steel casting via friction stir processing and subsequent annealing
	Xue, P; Li, WD; Wang, D; Wang, WG; Xiao, SL; Ma, ZY; Ma, ZY (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Peoples R China.
	2016-07-18
发表期刊	MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
ISSN	0921-5093
卷号	670 页码:153-158
摘要	This study provides an effective surface processing technology to increase the local mechanical properties of medium carbon steel castings. Ultrafine dual-phase structure of the ferrite and the martensite was obtained in the processed zone with a depth of 1 mm via submerged friction stir processing (FSP). Significantly enhanced yield strength (YS) of 2070 MPa was achieved in the FSP steel compared to that of the base material (BM) with a relatively low YS of 590 MPa, but a low uniform elongation (UE) of 3.0% was achieved compared to that of the BM (9.4%). After annealing, obvious carbide precipitation was observed in the original quenched martensite phases. Therefore, good strength-ductility synergies with high YS of 1020 MPa and 925 MPa, and acceptable UE of 5.9% and 9.3% were achieved in the FSP steel after annealed for 2 h at 500 degrees C and 600 degrees C, respectively. (C) 2016 Elsevier B.V. All rights reserved.
部门归属	[xue, p. ; li, w. d. ; wang, d. ; wang, w. g. ; xiao, b. l. ; ma, z. y.] chinese acad sci, inst met res, shenyang natl lab mat sci, 72 wenhua rd, shenyang 110016, peoples r china ; [li, w. d.] kocel grp ltd, 199 south tongxin st, yinchuan 750021, peoples r china
关键词	Friction Stir Processing Ultrafine-grained Structure Medium Carbon Steel Microstructure Mechanical Property
学科领域	Nanoscience & Nanotechnology ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
资助者	National Natural Science Foundation of China [51301178, 51331008, 51201163]
收录类别	sci
语种	英语
WOS记录号	WOS:000380078800019
引用统计	被引频次：34[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/76325
专题	中国科学院金属研究所
通讯作者	Ma, ZY (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Peoples R China.
推荐引用方式 GB/T 7714	Xue, P,Li, WD,Wang, D,et al. Enhanced mechanical properties of medium carbon steel casting via friction stir processing and subsequent annealing[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2016,670:153-158.
APA	Xue, P.,Li, WD.,Wang, D.,Wang, WG.,Xiao, SL.,...&Ma, ZY .(2016).Enhanced mechanical properties of medium carbon steel casting via friction stir processing and subsequent annealing.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,670,153-158.
MLA	Xue, P,et al."Enhanced mechanical properties of medium carbon steel casting via friction stir processing and subsequent annealing".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 670(2016):153-158.