题名: Secondary Precipitation Behavior of Nitride in the Electro-slag Remelted Structure of Alloy 690
作者: Wang, Min;  Chen, Bo;  Hao, Xian-Chao;  Ma, Ying-Che;  Liu, Kui
发表日期: 2017-8-1
摘要: The precipitation and evolution of secondary nitrides (S-nitrides) in the Alloy 690 electro-slag remelted (ESR) structure were investigated. Experimental results indicate that S-nitrides precipitated in the interdendritic region of the ESR structure at temperatures higher than 1100 degrees C. S-nitrides could spread throughout the entire interdendritic area after sufficient exposure, and they were more numerous and much finer than primary nitrides. Furthermore, after studying the evolution of S-nitride particles at 1100, 1200 and 1300 degrees C, it was determined that the precipitation of S-nitrides was controlled by the diffusion of nitrogen. In addition, by investigating the elemental segregation of ESR structure and calculating critical Ti concentrations, S-nitride precipitation was found to be thermodynamically inevitable in the Alloy 690 ESR structure.
刊名: ACTA METALLURGICA SINICA-ENGLISH LETTERS
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Wang, Min,Chen, Bo,Hao, Xian-Chao,et al. Secondary Precipitation Behavior Of Nitride In The Electro-slag Remelted Structure Of Alloy 690[J]. Acta Metallurgica Sinica-english Letters,2017,30(8):771-780.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Wang, Min]'s Articles
 [Chen, Bo]'s Articles
 [Hao, Xian-Chao]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Wang, Min]‘s Articles
 [Chen, Bo]‘s Articles
 [Hao, Xian-Chao]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2017  中国科学院金属研究所  -Feedback
Powered by CSpace