Initial Oxidation Behavior of Ferritic Stainless Steel with Sputtered Mn-Cu Coating

IMR OpenIR

	Initial Oxidation Behavior of Ferritic Stainless Steel with Sputtered Mn-Cu Coating
	Geng, Shujiang; Zhao, Qingqing; Wang, Hechang; Wang, Fuhui; Geng, SJ (reprint author), Northeastern Univ, Sch Met, 3-11 Wenhua Rd, Shenyang 110819, Peoples R China.; Geng, SJ (reprint author), Chinese Acad Sci, Inst Met Res, 62 Wencui Rd, Shenyang 110016, Peoples R China.
	2017-08-01
发表期刊	OXIDATION OF METALS
ISSN	0030-770X
卷号	88 期号:1 页码:203-210
摘要	Initial oxidation behavior of SUS 430 steel with a sputtered Mn-Cu coating was investigated in air at 800 A degrees C. It was found that Mn was preferrentially oxidized upon thermal exposure from 2 to 10 min. The surface scale mainly consisted of MnO inner layer and Mn3O4 outer layer, although a small amount of Fe was observable in the scale. In addition, CuO developed on the outer surface of the scale after 10 min of oxidation. However, the scale formed on the coated steel upon oxidation for 20-300 min was obviously different from that upon oxidation for 2-10 min. It was composed of a tri-layer containing a top layer of CuO, a middle layer of (Mn,Cu)(3)O-4 with some Fe, and an inner layer of Cr-rich oxide from the outer surface to the interface between scale and steel. With increasing oxidation time, furthermore, the top layer of CuO thickened first and then became thin. The oxidation mechanism was discussed.; Initial oxidation behavior of SUS 430 steel with a sputtered Mn-Cu coating was investigated in air at 800 A degrees C. It was found that Mn was preferrentially oxidized upon thermal exposure from 2 to 10 min. The surface scale mainly consisted of MnO inner layer and Mn3O4 outer layer, although a small amount of Fe was observable in the scale. In addition, CuO developed on the outer surface of the scale after 10 min of oxidation. However, the scale formed on the coated steel upon oxidation for 20-300 min was obviously different from that upon oxidation for 2-10 min. It was composed of a tri-layer containing a top layer of CuO, a middle layer of (Mn,Cu)(3)O-4 with some Fe, and an inner layer of Cr-rich oxide from the outer surface to the interface between scale and steel. With increasing oxidation time, furthermore, the top layer of CuO thickened first and then became thin. The oxidation mechanism was discussed.
部门归属	[geng, shujiang ; zhao, qingqing ; wang, hechang] northeastern univ, sch met, 3-11 wenhua rd, shenyang 110819, peoples r china ; [geng, shujiang ; wang, fuhui] chinese acad sci, inst met res, 62 wencui rd, shenyang 110016, peoples r china
关键词	Early Stage Thermal Exposure Steel With Mn-cu Coating Oxidation Mechanism
学科领域	Metallurgy & Metallurgical Engineering
资助者	National Natural Science Foundation of China (NSFC) [51371048]; National Key Basic Research Program of China (973 Program) [2012CB625100]
收录类别	SCI
语种	英语
WOS记录号	WOS:000404732500019
引用统计	被引频次：4[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/78029
专题	中国科学院金属研究所
通讯作者	Geng, SJ (reprint author), Northeastern Univ, Sch Met, 3-11 Wenhua Rd, Shenyang 110819, Peoples R China.; Geng, SJ (reprint author), Chinese Acad Sci, Inst Met Res, 62 Wencui Rd, Shenyang 110016, Peoples R China.
推荐引用方式 GB/T 7714	Geng, Shujiang,Zhao, Qingqing,Wang, Hechang,et al. Initial Oxidation Behavior of Ferritic Stainless Steel with Sputtered Mn-Cu Coating[J]. OXIDATION OF METALS,2017,88(1):203-210.
APA	Geng, Shujiang,Zhao, Qingqing,Wang, Hechang,Wang, Fuhui,Geng, SJ ,&Geng, SJ .(2017).Initial Oxidation Behavior of Ferritic Stainless Steel with Sputtered Mn-Cu Coating.OXIDATION OF METALS,88(1),203-210.
MLA	Geng, Shujiang,et al."Initial Oxidation Behavior of Ferritic Stainless Steel with Sputtered Mn-Cu Coating".OXIDATION OF METALS 88.1(2017):203-210.