题名: Eliminating detrimental effect of cold working on pitting corrosion resistance in high nitrogen austenitic stainless steels
作者: Wang, Qingchuan;  Zhang, Bingchun;  Ren, Yibin;  Yang, Ke
发表日期: 2017-7-15
摘要: The detrimental effect of cold working on pitting corrosion resistance was surprisingly found totally eliminated in high nitrogen stainless steels (HNS) with higher nitrogen content (0.92 wt.%) by electrochemical tests in chloride solution. Inclusions morphology and microstructure of cold-worked HNS were investigated. Then the passive film on HNS was analyzed by secondary ion mass spectroscopy (SIMS). For the first time nitrogen enrichment as a form of short range ordered [CrN] was observed in the chromium oxide layer of passive film on HNS. A possible reaction involving nitrogen enrichment is proposed to elucidate this exceptional behavior of corrosion resistance for HNS.
刊名: CORROSION SCIENCE
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Wang, Qingchuan,Zhang, Bingchun,Ren, Yibin,et al. Eliminating Detrimental Effect Of Cold Working On Pitting Corrosion Resistance In High Nitrogen Austenitic Stainless Steels[J]. Corrosion Science,2017,123:351-355.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Wang, Qingchuan]'s Articles
 [Zhang, Bingchun]'s Articles
 [Ren, Yibin]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Wang, Qingchuan]‘s Articles
 [Zhang, Bingchun]‘s Articles
 [Ren, Yibin]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2017  中国科学院金属研究所  -Feedback
Powered by CSpace