Thermo-mechanical fatigue property and life prediction of vermicular graphite iron

IMR OpenIR

	Thermo-mechanical fatigue property and life prediction of vermicular graphite iron
	Zhang, M. X.; Pang, J. C.; Qiu, Y.; Li, S. X.; Wang, M.; Zhang, Z. F.; Pang, JC; Zhang, ZF (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Peoples R China.
	2017-06-20
发表期刊	MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
ISSN	0921-5093
卷号	698 页码:63-72
摘要	Thermo-mechanical fatigue (TMF) failure is the major problem of the cylinder head subjected to combined variations in temperature and loading during operation. This study mainly focuses on the TMF property and the life prediction of vermicular graphite iron (VGI). The ferrite clusters can be easily found from the microstructure and fractography images. Compared with the TMF experimental data testing at 125-400 degrees C and 125-500 degrees C, significant cyclic hardening occurs in the former and slight hardening does in the latter. Depending on the difference in the damage mechanism between TMF and iso-thermal low-cycle fatigue (LCF), based on the hysteresis energy, a life prediction method has been proposed at first. By the minimum amount of LCF and TMF tests, the present method can predict the TMF life rapidly, accurately and cheaply. And based on the difference in the fatigue crack propagation thresholds between pearlite and ferrite, the fracture mechanism of TMF was also discussed.; Thermo-mechanical fatigue (TMF) failure is the major problem of the cylinder head subjected to combined variations in temperature and loading during operation. This study mainly focuses on the TMF property and the life prediction of vermicular graphite iron (VGI). The ferrite clusters can be easily found from the microstructure and fractography images. Compared with the TMF experimental data testing at 125-400 degrees C and 125-500 degrees C, significant cyclic hardening occurs in the former and slight hardening does in the latter. Depending on the difference in the damage mechanism between TMF and iso-thermal low-cycle fatigue (LCF), based on the hysteresis energy, a life prediction method has been proposed at first. By the minimum amount of LCF and TMF tests, the present method can predict the TMF life rapidly, accurately and cheaply. And based on the difference in the fatigue crack propagation thresholds between pearlite and ferrite, the fracture mechanism of TMF was also discussed.
部门归属	[zhang, m. x. ; pang, j. c. ; qiu, y. ; li, s. x. ; wang, m. ; zhang, z. f.] chinese acad sci, inst met res, shenyang natl lab mat sci, 72 wenhua rd, shenyang 110016, peoples r china
关键词	Thermo-mechanical Fatigue Vermicular Graphite Iron Life Prediction Fracture Mechanism
学科领域	Nanoscience & Nanotechnology ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
资助者	National Natural Science Foundation of China (NSFC) [51331007]
收录类别	SCI
语种	英语
WOS记录号	WOS:000405251900008
引用统计	被引频次：43[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/78082
专题	中国科学院金属研究所
通讯作者	Pang, JC; Zhang, ZF (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Peoples R China.
推荐引用方式 GB/T 7714	Zhang, M. X.,Pang, J. C.,Qiu, Y.,et al. Thermo-mechanical fatigue property and life prediction of vermicular graphite iron[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2017,698:63-72.
APA	Zhang, M. X..,Pang, J. C..,Qiu, Y..,Li, S. X..,Wang, M..,...&Zhang, ZF .(2017).Thermo-mechanical fatigue property and life prediction of vermicular graphite iron.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,698,63-72.
MLA	Zhang, M. X.,et al."Thermo-mechanical fatigue property and life prediction of vermicular graphite iron".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 698(2017):63-72.