题名: Effect of Nb on the Corrosion Resistance of Ni-Cr-Fe-Based Weld Metals
作者: Zhang, Xu;  Li, Dianzhong;  Li, Yiyi;  Lu, Shanping
发表日期: 2017-6-1
摘要: The localized corrosion behaviors (intergranular corrosion, pitting, and interdendritic corrosion) of Ni-Cr-Fe-based weld metals with different niobium concentrations were investigated both in the as-welded and heat-treated conditions using the modified Huey test (ASTM A262-2010). Results indicated that Nb could reduce the intergranular corrosion susceptibility of Ni-Cr-Fe-based weld metals by preventing Cr carbides from precipitating at grain boundaries. However, the degree of pitting corrosion became more severe with the increase of Nb. The Laves phase could be corroded easily in the oxidizing environment, which increased the pitting corrosion sensitivity of weld metals. Interdendritic corrosion became the main corrosion type of weld metals that were heat treated at 620 degrees C for 29 h. The depletions of elements Cr and Ni occurred in the interdendritic region, which resulted in the interdendritic corrosion of the heat-treated weld metals. With increasing Nb, the degree of Cr and Ni depletions became higher and the interdendritic corrosion sensitivity of the heat-treated weld metals increased.
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.

Recommended Citation:
Zhang, Xu,Li, Dianzhong,Li, Yiyi,et al. Effect Of Nb On The Corrosion Resistance Of Ni-cr-fe-based Weld Metals[J]. Corrosion,2017,73(6):734-741.

SCI Citaion Data:
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Zhang, Xu]'s Articles
 [Li, Dianzhong]'s Articles
 [Li, Yiyi]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Zhang, Xu]‘s Articles
 [Li, Dianzhong]‘s Articles
 [Li, Yiyi]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to  Add to Digg  Add to Reddit 
所有评论 (0)
内 容:
Email:  *
验证码:   刷新
标 题:
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.



Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace