Effect of Cu on corrosion behavior of low alloy steel under the simulated bottom plate environment of cargo oil tank

IMR OpenIR

	Effect of Cu on corrosion behavior of low alloy steel under the simulated bottom plate environment of cargo oil tank
	Hao, Xuehui; Dong, Junhua; Wei, Jie; Etim, Ini-Ibehe Nabuk; Ke, Wei; Dong, JH (reprint author), Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China.
	2017-06-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	121 页码:84-93
摘要	The effect of Cu on the corrosion behavior of low alloy steel under the simulated bottom plate environment of cargo oil tank was investigated by using gravimetric test, SEM, EDS, XPS, XRD and electrochemical measurements. The results indicate that the corrosion resistance of 16MnCu steel was higher than that of 16Mn steel, which was related to the deposition of nano-sized Cu particles on the surface. The deposited Cu might suppress both the anodic dissolution of the ferrite and hydrogen evolution reaction on the cementite, leading to the reduction of the galvanic effect caused by the residual cementite. (C) 2017 Elsevier Ltd. All rights reserved.; The effect of Cu on the corrosion behavior of low alloy steel under the simulated bottom plate environment of cargo oil tank was investigated by using gravimetric test, SEM, EDS, XPS, XRD and electrochemical measurements. The results indicate that the corrosion resistance of 16MnCu steel was higher than that of 16Mn steel, which was related to the deposition of nano-sized Cu particles on the surface. The deposited Cu might suppress both the anodic dissolution of the ferrite and hydrogen evolution reaction on the cementite, leading to the reduction of the galvanic effect caused by the residual cementite. (C) 2017 Elsevier Ltd. All rights reserved.
部门归属	[hao, xuehui ; dong, junhua ; wei, jie ; etim, ini-ibehe nabuk ; ke, wei] chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china
关键词	Cu Steel Sem Xrd Eis
学科领域	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
资助者	National Natural Science Foundation of China [51471175, 51501201]
收录类别	SCI
语种	英语
WOS记录号	WOS:000401597700008
引用统计	被引频次：39[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/78115
专题	中国科学院金属研究所
通讯作者	Dong, JH (reprint author), Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China.
推荐引用方式 GB/T 7714	Hao, Xuehui,Dong, Junhua,Wei, Jie,et al. Effect of Cu on corrosion behavior of low alloy steel under the simulated bottom plate environment of cargo oil tank[J]. CORROSION SCIENCE,2017,121:84-93.
APA	Hao, Xuehui,Dong, Junhua,Wei, Jie,Etim, Ini-Ibehe Nabuk,Ke, Wei,&Dong, JH .(2017).Effect of Cu on corrosion behavior of low alloy steel under the simulated bottom plate environment of cargo oil tank.CORROSION SCIENCE,121,84-93.
MLA	Hao, Xuehui,et al."Effect of Cu on corrosion behavior of low alloy steel under the simulated bottom plate environment of cargo oil tank".CORROSION SCIENCE 121(2017):84-93.