题名: Stress corrosion cracking of fusion boundary for 316L/52M dissimilar metal weld joints in borated and lithiated high temperature water
作者: Zhu, Ruolin;  Wang, Jianqiu;  Zhang, Zhiming;  Han, En-Hou
发表日期: 2017-5-15
摘要: The stress corrosion cracking (SCC) crack growth rates (CGRs) at the fusion boundary (FB) for 316L/52M weld joints were measured using direct current potential drop systems in borated and lithiated high temperature water. The cracks propagated along the FB and were blocked after propagating into the composition transient zone. The cracking mode is both intergranular and transgranular. The CGRs at the FB are similar to those in the heat-affected zone (HAZ) in oxygenated water, but slightly higher than those in the HAZ in hydrogenated water. The temperature dependences of CGR in both hydrogenated and oxygenated water are discussed. (C) 2017 Elsevier Ltd. All rights reserved.
刊名: CORROSION SCIENCE
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Zhu, Ruolin,Wang, Jianqiu,Zhang, Zhiming,et al. Stress Corrosion Cracking Of Fusion Boundary For 316l/52m Dissimilar Metal Weld Joints In Borated And Lithiated High Temperature Water[J]. Corrosion Science,2017,120:219-230.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Zhu, Ruolin]'s Articles
 [Wang, Jianqiu]'s Articles
 [Zhang, Zhiming]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Zhu, Ruolin]‘s Articles
 [Wang, Jianqiu]‘s Articles
 [Zhang, Zhiming]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2017  中国科学院金属研究所  -Feedback
Powered by CSpace