Corrosion resistance of chromised and aluminised coatings in wet CO2 gas at 650 degrees C
Thuan Dinh Nguyen; Peng, Xiao; Zhang, Jianqiang; Young, David J.; Young, DJ (reprint author), Univ New South Wales, Sch Mat Sci & Engn, Sydney, NSW 2052, Australia.
2017-04-25
发表期刊SURFACE & COATINGS TECHNOLOGY
ISSN0257-8972
卷号316页码:226-238
摘要Four chromised and aluminised coatings, with and without an intermediate nickel layer, were produced by pack cementation. The nickel layer was deposited onto a T91 steel substrate prior to the pack cementation process to limit interdiffusion of elements between the coatings and the substrate. The coated and uncoated steels were exposed to Ar-20CO(2)-20H(2)O gas at 650 degrees C. The uncoated steel formed a thick, iron-rich oxide scale, whereas all coated samples formed thin, protective chromia or alumina scales. The uncoated steel was carburised under its scale. Carbide precipitates were formed in the chromized coatings before and after reactions, but not in the aluminised coatings. (C) 2017 Elsevier B.V. All rights reserved.; Four chromised and aluminised coatings, with and without an intermediate nickel layer, were produced by pack cementation. The nickel layer was deposited onto a T91 steel substrate prior to the pack cementation process to limit interdiffusion of elements between the coatings and the substrate. The coated and uncoated steels were exposed to Ar-20CO(2)-20H(2)O gas at 650 degrees C. The uncoated steel formed a thick, iron-rich oxide scale, whereas all coated samples formed thin, protective chromia or alumina scales. The uncoated steel was carburised under its scale. Carbide precipitates were formed in the chromized coatings before and after reactions, but not in the aluminised coatings. (C) 2017 Elsevier B.V. All rights reserved.
部门归属[thuan dinh nguyen ; zhang, jianqiang ; young, david j.] univ new south wales, sch mat sci & engn, sydney, nsw 2052, australia ; [peng, xiao] inst met sci & technol, state key lab corros & protect, shenyang, peoples r china
关键词Pack Cementation Diffusion Coatings Co2 Corrosion
学科领域Materials Science, Coatings & Films ; Physics, Applied
资助者Early Career Research Grant (University of New South Wales) [PS40715]
收录类别SCI
语种英语
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/78177
专题中国科学院金属研究所
通讯作者Young, DJ (reprint author), Univ New South Wales, Sch Mat Sci & Engn, Sydney, NSW 2052, Australia.
推荐引用方式
GB/T 7714
Thuan Dinh Nguyen,Peng, Xiao,Zhang, Jianqiang,et al. Corrosion resistance of chromised and aluminised coatings in wet CO2 gas at 650 degrees C[J]. SURFACE & COATINGS TECHNOLOGY,2017,316:226-238.
APA Thuan Dinh Nguyen,Peng, Xiao,Zhang, Jianqiang,Young, David J.,&Young, DJ .(2017).Corrosion resistance of chromised and aluminised coatings in wet CO2 gas at 650 degrees C.SURFACE & COATINGS TECHNOLOGY,316,226-238.
MLA Thuan Dinh Nguyen,et al."Corrosion resistance of chromised and aluminised coatings in wet CO2 gas at 650 degrees C".SURFACE & COATINGS TECHNOLOGY 316(2017):226-238.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Thuan Dinh Nguyen]的文章
[Peng, Xiao]的文章
[Zhang, Jianqiang]的文章
百度学术
百度学术中相似的文章
[Thuan Dinh Nguyen]的文章
[Peng, Xiao]的文章
[Zhang, Jianqiang]的文章
必应学术
必应学术中相似的文章
[Thuan Dinh Nguyen]的文章
[Peng, Xiao]的文章
[Zhang, Jianqiang]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。