题名: Microstructure, Tensile Properties, and Hot-Working Characteristics of a Hot Isostatic-Pressed Powder Metallurgy Superalloy
作者: Chang, Litao;  Sun, Wenru;  Cui, Yuyou;  Yang, Rui
发表日期: 2017-3-1
摘要: A series of microstructure observation, tensile, and hot compression tests were conducted to investigate the variation of microstructure, tensile properties, and hot-working characteristics of a powder metallurgy (PM) superalloy with hot isostatic pressing (HIPing) temperature, to establish a basis for the parameter selection for PM superalloy preparation. The results show that the dendritic structure from the powder was not completely removed until the HIPing temperature is above the gamma' solvus; gamma/gamma' eutectic formed when the powder particles were HIPed at 1533 K (1260 A degrees C) or above. Prior particle boundaries (PPBs) were observed in alloys HIPed at 1513 K (1240 A degrees C) and below; the PPB decoration is serious in alloys HIPed at 1483 K and 1513 K (1210 A degrees C and 1240 A degrees C), owing to melting and aggregation of the boride phase at the particle boundaries during HIPing; the PPBs were eliminated when the HIPing was done at 1533 K (1260 A degrees C) or above. Tensile fracture mode of the alloy changes from inter-particle and transgranular mixed fracture to transgranular fracture with increasing HIPing temperature, which is in accordance with the change in precipitate distribution at the PPBs. The hot workability of alloy is poor for all combinations of HIPing/deformation conditions except for HIPing at sub-solvus temperature and deformation at low strain rates. (C) The Minerals, Metals & Materials Society and ASM International 2016
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.

Recommended Citation:
Chang, Litao,Sun, Wenru,Cui, Yuyou,et al. Microstructure, Tensile Properties, And Hot-working Characteristics Of A Hot Isostatic-pressed Powder Metallurgy Superalloy[J]. Metallurgical And Materials Transactions A-physical Metallurgy And Materials Science,2017,48a(3):1273-1287.

SCI Citaion Data:
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Chang, Litao]'s Articles
 [Sun, Wenru]'s Articles
 [Cui, Yuyou]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Chang, Litao]‘s Articles
 [Sun, Wenru]‘s Articles
 [Cui, Yuyou]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to  Add to Digg  Add to Reddit 
所有评论 (0)
内 容:
Email:  *
验证码:   刷新
标 题:
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.



Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace