Creep properties of a powder metallurgy disk superalloy at 700 degrees C
Dong, Kaixin; Yuan, Chao; Gao, Shuang; Jia, Chonglin; Guo, Jianting; Ge, Changchun; Yuan, C (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China.
2017-02-01
发表期刊JOURNAL OF MATERIALS RESEARCH
ISSN0884-2914
卷号32期号:3页码:624-633
摘要As the operating temperature of disk service was elevated from 650 degrees C to 700 degrees C, the creep properties urged to be paid attention. To investigate the creep properties of spray-formed low solvus, high refractory (LSHR) superalloy at about 700 degrees C, creep tests were conducted under seven different stress ranging from 690 MPa to 897 MPa. By means of creep curves and fracture microstructure observation, the creep behaviors and fracture mechanisms of spray-formed LSHR were analyzed. Stress exponent of the alloy was comparable to other disk superalloys such as Waspaloy and Inconel 718. It was interesting to find a transition in the creep behavior in two stress regimes. The contribution of grain boundary sliding in the low stress regime was greater than that in the higher stress. Under higher stress microcracks initiated along the intragranular slip bands because of strain concentration. The spray-forming LSHR exhibited a good creep resistance at low stress compared with other two superalloys by using Larson-Miller parameter, which was consistent with the transition of fracture behaviors.; As the operating temperature of disk service was elevated from 650 degrees C to 700 degrees C, the creep properties urged to be paid attention. To investigate the creep properties of spray-formed low solvus, high refractory (LSHR) superalloy at about 700 degrees C, creep tests were conducted under seven different stress ranging from 690 MPa to 897 MPa. By means of creep curves and fracture microstructure observation, the creep behaviors and fracture mechanisms of spray-formed LSHR were analyzed. Stress exponent of the alloy was comparable to other disk superalloys such as Waspaloy and Inconel 718. It was interesting to find a transition in the creep behavior in two stress regimes. The contribution of grain boundary sliding in the low stress regime was greater than that in the higher stress. Under higher stress microcracks initiated along the intragranular slip bands because of strain concentration. The spray-forming LSHR exhibited a good creep resistance at low stress compared with other two superalloys by using Larson-Miller parameter, which was consistent with the transition of fracture behaviors.
部门归属[dong, kaixin ; yuan, chao ; gao, shuang ; guo, jianting] chinese acad sci, inst met res, shenyang 110016, peoples r china ; [jia, chonglin ; ge, changchun] univ sci & technol beijing, sch mat sci & engn, beijing 100083, peoples r china
学科领域Materials Science, Multidisciplinary
资助者Technical Support Division of Shenyang R & D Center for Advanced Materials
收录类别SCI
语种英语
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/78301
专题中国科学院金属研究所
通讯作者Yuan, C (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China.
推荐引用方式
GB/T 7714
Dong, Kaixin,Yuan, Chao,Gao, Shuang,et al. Creep properties of a powder metallurgy disk superalloy at 700 degrees C[J]. JOURNAL OF MATERIALS RESEARCH,2017,32(3):624-633.
APA Dong, Kaixin.,Yuan, Chao.,Gao, Shuang.,Jia, Chonglin.,Guo, Jianting.,...&Yuan, C .(2017).Creep properties of a powder metallurgy disk superalloy at 700 degrees C.JOURNAL OF MATERIALS RESEARCH,32(3),624-633.
MLA Dong, Kaixin,et al."Creep properties of a powder metallurgy disk superalloy at 700 degrees C".JOURNAL OF MATERIALS RESEARCH 32.3(2017):624-633.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Dong, Kaixin]的文章
[Yuan, Chao]的文章
[Gao, Shuang]的文章
百度学术
百度学术中相似的文章
[Dong, Kaixin]的文章
[Yuan, Chao]的文章
[Gao, Shuang]的文章
必应学术
必应学术中相似的文章
[Dong, Kaixin]的文章
[Yuan, Chao]的文章
[Gao, Shuang]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。