题名: Natural ageing responses of duplex structured Mg-Li based alloys
作者: Li, C. Q.;  Xu, D. K.;  Wang, B. J.;  Sheng, L. Y.;  Qiao, Y. X.;  Han, E. H.
发表日期: 2017-1-5
摘要: Natural ageing responses of duplex structured Mg-6% Li and Mg-6% Li-6% Zn-1.2% Y alloys have been investigated. Microstructural analyses revealed that the precipitation and coarsening process of alpha-Mg particles could occur in beta-Li phases of both two alloys during ageing process. Since a certain amount of Mg atoms in beta-Li phases were consumed for the precipitation of abundant tiny MgLiZn particles, the size of alpha-Mg precipitates in Mg-6% Li-6% Zn-1.2% Y alloy was relatively smaller than that in Mg-6% Li alloy. Micro hardness measurements demonstrated that with the ageing time increasing, the alpha-Mg phases in Mg-6% Li alloy could have a constant hardness value of 41 HV, but the contained beta-Li phases exhibited a slight age-softening response. Compared with the Mg-6% Li alloy, the age-softening response of beta-Li phases in Mg-6% Li-6% Zn-1.2% Y alloy was much more profound. Meanwhile, a normal age-hardening response of alpha-Mg phases was maintained. Tensile results indicated that obvious ageing-softening phenomenon in terms of macro tensile strength occurred in both two alloys. Failure analysis demonstrated that for the Mg-6% Li alloy, cracks were preferentially initiated at alpha-Mg/beta-Li interfaces. For the Mg-6% Li-6% Zn-1.2% Y alloy, cracks occurred at both alpha-Mg/beta-Li interfaces and slip bands in alpha-Mg and beta-Li phases.
刊名: SCIENTIFIC REPORTS
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Li, C. Q.,Xu, D. K.,Wang, B. J.,et al. Natural Ageing Responses Of Duplex Structured Mg-li Based Alloys[J]. Scientific Reports,2017,7:-.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Li, C. Q.]'s Articles
 [Xu, D. K.]'s Articles
 [Wang, B. J.]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Li, C. Q.]‘s Articles
 [Xu, D. K.]‘s Articles
 [Wang, B. J.]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace