题名: Multi-Gating Injection Molding to Enhance the Thermal Conductivity of Carbon Fiber/Polysulfone Composite
作者: Sun, Deliang;  Lin, Guoming;  Sui, Guoxin;  Hao, Yulin;  Yang, Rui;  Zhang, Kai
发表日期: 2017
摘要: Carbon fiber was blended into the polysulfone matrix by twin screw extruder. The polymer composites samples were prepared using four different processing technologies, the compression molding, edge-gating injection molding, sprue-gating injection molding, and the multi-gating injection molding techniques. Among four techniques, the composite samples manufactured by multi-gating injection molding technique got a higher value of thermal conductivity, which is due to the carbon fibers orientation and distribution. The experimental result indicated that the fiber orientation have a significant influence on the thermal conductivity of polymer composites. The thermal conductivity of sample made by multi-gating injection molding was 1.82 W/(m.K)when the fiber content was 26 vol%, which was nearly twice than the values obtained by conventional technologies. (C) 2015 Society of Plastics Engineers
刊名: POLYMER COMPOSITES
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Sun, Deliang,Lin, Guoming,Sui, Guoxin,et al. Multi-gating Injection Molding To Enhance The Thermal Conductivity Of Carbon Fiber/polysulfone Composite[J]. Polymer Composites,2017,38(1):185-191.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Sun, Deliang]'s Articles
 [Lin, Guoming]'s Articles
 [Sui, Guoxin]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Sun, Deliang]‘s Articles
 [Lin, Guoming]‘s Articles
 [Sui, Guoxin]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace