Cold Cracking Sensitivity of a Newly Developed 9Cr2WVTa Steel

IMR OpenIR

	Cold Cracking Sensitivity of a Newly Developed 9Cr2WVTa Steel
	Wang, Jian; Lu, Shanping; Li, Yongkui; Hu, Qingxian; Rong, Lijian; Li, Dianzhong; Lu, SP (reprint author), Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China.; Lu, SP (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China.
	2017
发表期刊	JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
ISSN	1059-9495
卷号	26 期号:1 页码:258-267
摘要	Cold cracking susceptibility of the newly developed 9Cr2WVTa steel plate welded with the corresponding gas tungsten arc welding wire has been evaluated using the implant test and the Y-groove cracking test. Measurement of diffusible hydrogen content shows that the welding wire is ultra-low welding consumables (0.40 mL/100 g). Results of the implant test show that the fracture critical stress without pre-heating is only 300 MPa and increases up to the yield strength with pre-heating to 150 A degrees C. The fracture critical stress under high heat input decreases to 250 MPa owing to the formation of quenched microstructure. Fractographies show ductile dimple fracture under higher loads and quasi-cleavage fracture under lower loads. Results of Y-groove cracking tests show that the minimum pre-heating temperature is 150 A degrees C and the maximum transverse residual stress is located at the root of the weld metal. Therefore, the heat input should be chosen in a proper range and the pre-heating temperature is no less than 150 A degrees C.; Cold cracking susceptibility of the newly developed 9Cr2WVTa steel plate welded with the corresponding gas tungsten arc welding wire has been evaluated using the implant test and the Y-groove cracking test. Measurement of diffusible hydrogen content shows that the welding wire is ultra-low welding consumables (0.40 mL/100 g). Results of the implant test show that the fracture critical stress without pre-heating is only 300 MPa and increases up to the yield strength with pre-heating to 150 A degrees C. The fracture critical stress under high heat input decreases to 250 MPa owing to the formation of quenched microstructure. Fractographies show ductile dimple fracture under higher loads and quasi-cleavage fracture under lower loads. Results of Y-groove cracking tests show that the minimum pre-heating temperature is 150 A degrees C and the maximum transverse residual stress is located at the root of the weld metal. Therefore, the heat input should be chosen in a proper range and the pre-heating temperature is no less than 150 A degrees C.
部门归属	[wang, jian ; lu, shanping ; li, yongkui ; li, dianzhong] chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china ; [wang, jian ; lu, shanping ; rong, lijian] chinese acad sci, inst met res, key lab nucl mat & safety assessment, shenyang 110016, peoples r china ; [hu, qingxian] jiangsu univ sci & technol, jiangsu prov key lab adv welding technol, zhenjiang 212003, peoples r china
关键词	Cold Cracking Diffusible Hydrogen Implant Test Modeling And Simulation Steel Y-groove Cracking Test
学科领域	Materials Science, Multidisciplinary
资助者	National Natural Science Foundation of China [91226204]; Chinese Academy of Science [XDA03010304]
收录类别	SCI
语种	英语
WOS记录号	WOS:000393108200030
引用统计	被引频次：3[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/78371
专题	中国科学院金属研究所
通讯作者	Lu, SP (reprint author), Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China.; Lu, SP (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China.
推荐引用方式 GB/T 7714	Wang, Jian,Lu, Shanping,Li, Yongkui,et al. Cold Cracking Sensitivity of a Newly Developed 9Cr2WVTa Steel[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,2017,26(1):258-267.
APA	Wang, Jian.,Lu, Shanping.,Li, Yongkui.,Hu, Qingxian.,Rong, Lijian.,...&Lu, SP .(2017).Cold Cracking Sensitivity of a Newly Developed 9Cr2WVTa Steel.JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,26(1),258-267.
MLA	Wang, Jian,et al."Cold Cracking Sensitivity of a Newly Developed 9Cr2WVTa Steel".JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE 26.1(2017):258-267.