题名: A study of epitaxial growth behaviors of equiaxed alpha phase at different cooling rates in near alpha titanium alloy
作者: Gao, Xiongxiong;  Zeng, Weidong;  Zhang, Saifei;  Wang, Qingjiang
发表日期: 2017
摘要: The epitaxial growth behaviors of equiaxed primary alpha phase (alpha(p)) at different cooling rates (150-0.15 degrees C/s) in a near alpha titanium alloy Ti60 were studied by optical micrograph, back scattered electron (BSE) images, high-resolution electron backscatter diffraction technique (EBSD) and electron probe micro-analysis (EPMA). Microstructural observations indicated that the size of alpha(p) significantly increased with decreasing cooling rate. The rim-alpha phase observed by BSE image, which formed at the periphery of ap during cooling and has an identical crystallographic orientation to the interior region of alpha(p) analyzed by Kikuchi diffraction patterns, is considered to be evidence of epitaxial growth of alpha(p). EBSD analysis also showed that ap preferentially grew extending for a distance along the WO boundary resulting in extension-alpha phase from alpha(p). The EPMA confirmed that contrast difference in BSE image within alpha(p) is caused by the difference in composition. The further microanalysis of local composition indicated that epitaxial growth during continuous cooling is mainly controlled by the diffusional redistribution of aluminum and molybdenum atoms between alpha(p) and 13 matrix. On this basis, the sizes of alpha(p) were theoretically calculated after continuous cooling based on a diffusion-controlled model, and model predictions showed good agreement with experimental measurements. (C) 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
刊名: ACTA MATERIALIA
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Gao, Xiongxiong,Zeng, Weidong,Zhang, Saifei,et al. A Study Of Epitaxial Growth Behaviors Of Equiaxed Alpha Phase At Different Cooling Rates In Near Alpha Titanium Alloy[J]. Acta Materialia,2017,122:298-309.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Gao, Xiongxiong]'s Articles
 [Zeng, Weidong]'s Articles
 [Zhang, Saifei]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Gao, Xiongxiong]‘s Articles
 [Zeng, Weidong]‘s Articles
 [Zhang, Saifei]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2017  中国科学院金属研究所  -Feedback
Powered by CSpace