Improvement of notch fatigue properties of ultra-high CM400 maraging steel through shot peening

IMR OpenIR

	Improvement of notch fatigue properties of ultra-high CM400 maraging steel through shot peening
	Duan, Qi-qiang; Wang, Bin; Zhang, Peng; Yang, Ke; Zhang, Zhe-Feng; Zhang, P; Zhang, ZF (reprint author), Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China.
	2017-12-14
发表期刊	CAMBRIDGE UNIV PRESS
ISSN	0884-2914
卷号	32 期号:23 页码:4424-4432
摘要	Shot-peened CM400 maraging steel was used to study the mechanism of enhanced notch fatigue properties of ultra-high strength materials. After shot peening, the specimen surface became rougher, but the transversal machining traces were reduced. The yield strength was slightly improved while the ultimate tensile strength and hardness maintained constant; as a result, the fatigue limit was promoted by about 1.5 times. The nucleated sites of the fatigue fracture were partly changed from the surface to subsurface/interior of the specimen. To further analyze the influencing factors of fatigue properties, the fatigue damage process may be resolved to two aspects: (a) fatigue damage rate affected by shear deformation and (b) fatigue damage tolerance controlled by the dilatation fracture process. Considering the stress state near the notch tip, the hydrostatic stress and maximum shear stress are considered for better understanding these two aspects. It is observed that the fatigue damage tolerance increased while the fatigue damage rate decreased after shot peening. Therefore, the notch fatigue properties of CM400 maraging steels can effectively be improved.; Shot-peened CM400 maraging steel was used to study the mechanism of enhanced notch fatigue properties of ultra-high strength materials. After shot peening, the specimen surface became rougher, but the transversal machining traces were reduced. The yield strength was slightly improved while the ultimate tensile strength and hardness maintained constant; as a result, the fatigue limit was promoted by about 1.5 times. The nucleated sites of the fatigue fracture were partly changed from the surface to subsurface/interior of the specimen. To further analyze the influencing factors of fatigue properties, the fatigue damage process may be resolved to two aspects: (a) fatigue damage rate affected by shear deformation and (b) fatigue damage tolerance controlled by the dilatation fracture process. Considering the stress state near the notch tip, the hydrostatic stress and maximum shear stress are considered for better understanding these two aspects. It is observed that the fatigue damage tolerance increased while the fatigue damage rate decreased after shot peening. Therefore, the notch fatigue properties of CM400 maraging steels can effectively be improved.
部门归属	[duan, qi-qiang ; wang, bin ; zhang, peng ; yang, ke ; zhang, zhe-feng] chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china
关键词	Fatigue Steel Strength
学科领域	Materials Science, Multidisciplinary
资助者	National Natural Science Foundation of China (NSFC) [51331007, 51301179]
收录类别	SCI
语种	英语
WOS记录号	WOS:000418368100015
引用统计	被引频次：15[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/78935
专题	中国科学院金属研究所
通讯作者	Zhang, P; Zhang, ZF (reprint author), Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China.
推荐引用方式 GB/T 7714	Duan, Qi-qiang,Wang, Bin,Zhang, Peng,et al. Improvement of notch fatigue properties of ultra-high CM400 maraging steel through shot peening[J]. CAMBRIDGE UNIV PRESS,2017,32(23):4424-4432.
APA	Duan, Qi-qiang.,Wang, Bin.,Zhang, Peng.,Yang, Ke.,Zhang, Zhe-Feng.,...&Zhang, ZF .(2017).Improvement of notch fatigue properties of ultra-high CM400 maraging steel through shot peening.CAMBRIDGE UNIV PRESS,32(23),4424-4432.
MLA	Duan, Qi-qiang,et al."Improvement of notch fatigue properties of ultra-high CM400 maraging steel through shot peening".CAMBRIDGE UNIV PRESS 32.23(2017):4424-4432.