题名: Effect of Surface Topography on Room Temperature Tensile Ductility of TiAl
作者: Lin, Bochao;  Liu, Renci;  Jia, Qing;  Cui, Yuyou;  Yang, Rui
发表日期: 2017-12-1
摘要: Room temperature tensile ductility of extruded Ti-47Al-1.5Nb-1Cr-1Mn-0.5B (at.%) with different surface topographies was investigated. Tensile specimens were subjected to grinding with sandpaper of different grits and electrolytic polishing to achieve different surface topographies. Surface morphology/topography and tensile ductility of different surface preparations were compared. Results show that for ground samples, when the mean amplitude deviation (Ra) exceeds 0.1 mu m, initiation of tensile failure transits from the sample interior to surface, and tensile fracture strain decreases linearly with increasing Ra. Electrolytic polishing improves the surface topography of TiAl not only by reducing Ra, but also by modifying the amplitude shape and distribution of the surface, and it therefore increases ductility. The present work suggests that surface amplitude deviation (Ra), skewness (Rsk) and kurtosis (Rku) are appropriate parameters to evaluate the surface topography of intermetallic materials with limited ductility such as TiAl.
刊名: SPRINGER
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Lin, Bochao,Liu, Renci,Jia, Qing,et al. Effect Of Surface Topography On Room Temperature Tensile Ductility Of Tial[J]. Springer,2017,69(12):2583-2587.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Lin, Bochao]'s Articles
 [Liu, Renci]'s Articles
 [Jia, Qing]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Lin, Bochao]‘s Articles
 [Liu, Renci]‘s Articles
 [Jia, Qing]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace