题名: The Intrinsic Relationship Between Microstructure Evolution and Thermal Fatigue Behavior of a Single-Crystal Cobalt-Base Superalloy
作者: Gui, Wei-Min;  Zhang, Hong-Yu;  Yang, Min;  Jin, Tao;  Sun, Xiao-Feng;  Zheng, Qi
发表日期: 2017-12-1
摘要: The intrinsic relationship between the microstructure evolution and thermal fatigue behavior of a single-crystal cobalt-base superalloy has been investigated. The thermal fatigue tests are performed cyclically between room temperature and 1050 degrees C using V-notch plate specimens. Three states of thermal fatigue specimens are selected: the as-cast, solutionized as well as aged states. The solution treatment is carried out at 1260 degrees C for 24 h, which results in the dissolution of most of interdendritic continuous primary carbides. The subsequent aging treatment is carried out at 1100 degrees C for 100 h after solution treatment, resulting in the precipitation of a profusion of chain- and point-like M23C6 carbides in the matrix. The results indicate that the heat treatment can improve the thermal fatigue properties of the alloy and the effect of the solution treatment is more prominent than that of the aging treatment. The coarse and continuously distributed primary carbides in the as-cast state are changed into small and discontinuous distribution by heat treatment, which is the dominant factor in the improvement of thermal fatigue property. Additionally, the effect of oxidation behavior during thermal fatigue test on the thermal fatigue behavior is also studied.
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.

Recommended Citation:
Gui, Wei-Min,Zhang, Hong-Yu,Yang, Min,et al. The Intrinsic Relationship Between Microstructure Evolution And Thermal Fatigue Behavior Of A Single-crystal Cobalt-base Superalloy[J]. Chinese Acad Sciences, Inst Metal Research,2017,30(12):1192-1200.

SCI Citaion Data:
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Gui, Wei-Min]'s Articles
 [Zhang, Hong-Yu]'s Articles
 [Yang, Min]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Gui, Wei-Min]‘s Articles
 [Zhang, Hong-Yu]‘s Articles
 [Yang, Min]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to  Add to Digg  Add to Reddit 
所有评论 (0)
内 容:
Email:  *
验证码:   刷新
标 题:
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.



Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace