题名: Synthesis of variously shaped magnetic FeCo nanoparticles and the growth mechanism of FeCo nanocubes
作者: Yuan, Jie;  Li, Cai-Fu;  Liu, Zhi-Quan;  Di Wu;  Cao, Lihua
发表日期: 2017-11-21
摘要: By varying the molar ratio of Fe2+/Co2+ and the concentration of PEG-400 and cyclohexane, as well as the reaction temperature and time, FeCo alloy nanoparticles with different morphologies have been synthesized successfully, in which the iron content could be adjusted in the range of 17-84 at%. Accompanying the decrease of the Fe2+/Co2+ molar ratio from 5 : 1 to 1 : 5, the shapes of FeCo nanoparticles change from sheets, cubes and spheres to flower-like particles, which were confirmed by X-ray powder diffraction, scanning electron microscopy and transmission electron microscopy. Typically, the growth direction of nanosheets is along the [110] direction exposing (110) surface planes, while FeCo nanocubes have a perfect square shape with clear-cut edges and expose {100} surface facets. It is found that the combined action of PEG-400 and cyclohexane plays a vital role in regulating the growth rate of different crystal facets. Under the assistance of PEG-400 and cyclohexane, the growth of perfect cubes with some intermediates can be observed. Their addition effects were discussed, and a "step-by-step surface wrapping" growth mechanism was proposed to illustrate the formation of nanocubes. Among different nanoparticles, Fe75Co25 nanocubes (250 +/- 10 nm) have the highest saturation magnetization, which is measured to be 250 emu g(-1).
刊名: ROYAL SOC CHEMISTRY
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Yuan, Jie,Li, Cai-Fu,Liu, Zhi-Quan,et al. Synthesis Of Variously Shaped Magnetic Feco Nanoparticles And The Growth Mechanism Of Feco Nanocubes[J]. Royal Soc Chemistry,2017,19(43):6506-6515.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Yuan, Jie]'s Articles
 [Li, Cai-Fu]'s Articles
 [Liu, Zhi-Quan]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Yuan, Jie]‘s Articles
 [Li, Cai-Fu]‘s Articles
 [Liu, Zhi-Quan]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace