题名: Effect of the Amount of Cold Work on Corrosion of Type 304 Nuclear Grade Stainless Steel in High-Temperature Water
作者: Deng, Ping;  Peng, Qunjia;  Han, En-Hou;  Ke, Wei
发表日期: 2017-10-1
摘要: Effect of the amount of cold work (CW) on corrosion of Type 304 nuclear grade stainless steel in high-temperature water was investigated. The investigation was conducted by comparing the microstructure of oxide scales formed on the steel subjected to different amounts of CW. The result revealed that increasing the amount of CW resulted in inhomogeneous thickness of the inner continuous oxide film, which was caused by the enhanced localized corrosion at the deformation band (DB) and the grain boundary (GB). Further, the localized corrosion rate at the DB was likely higher than that at the GB, which resulted from the difference in the composition of the oxide formed at the DB and GB.
刊名: NATL ASSOC CORROSION ENG
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Deng, Ping,Peng, Qunjia,Han, En-Hou,et al. Effect Of The Amount Of Cold Work On Corrosion Of Type 304 Nuclear Grade Stainless Steel In High-temperature Water[J]. Natl Assoc Corrosion Eng,2017,73(10):1237-1249.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Deng, Ping]'s Articles
 [Peng, Qunjia]'s Articles
 [Han, En-Hou]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Deng, Ping]‘s Articles
 [Peng, Qunjia]‘s Articles
 [Han, En-Hou]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace