Influence of Cr addition on the interface purification of vacuum brazed NiCr-Cr3C2 coatings on single crystal superalloy
Wang, D.; Wang, W. Q.; Chen, X. G.; Chi, C. T.; Wang, M. S.; Han, X.; Xie, Y. J.; Xie, YJ (reprint author), Jiangxi Acad Sci, Inst Appl Phys, Nanchang 330029, Jiangxi, Peoples R China.; Xie, YJ (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China.
2017-09-25
发表期刊ELSEVIER SCIENCE SA
ISSN0257-8972
卷号325页码:200-209
摘要In order to improve the high temperature wear- and oxidation resistance of single crystal superalloy, NiCr-Cr3C2 coatings were vacuum brazed on the surface. Different weight ratios of Cr were added into the coatings to control the diffusion of Si and C into the base metal, which would be harmful to the base metal stability. The results show that, when no Cr was added into the coatings, a layer of Ni3Si phase at the interface and MC precipitates in base metal were produced. With the increase of the Cr addition, the coating/base metal interface was gradually purified. The Ni3Si layer and the MC precipitates disappeared when the Cr addition increased to 30 wt% and an interface was clearly presented with the 'gamma' phases on both sides epitaxially growing on some extent. After 200 thermal fatigue cycles, the total crack lengths were measured, which decreased with increasing Cr addition, indicating that the thermal fatigue resistance was improved. (C) 2017 Elsevier B.V. All rights reserved.; In order to improve the high temperature wear- and oxidation resistance of single crystal superalloy, NiCr-Cr3C2 coatings were vacuum brazed on the surface. Different weight ratios of Cr were added into the coatings to control the diffusion of Si and C into the base metal, which would be harmful to the base metal stability. The results show that, when no Cr was added into the coatings, a layer of Ni3Si phase at the interface and MC precipitates in base metal were produced. With the increase of the Cr addition, the coating/base metal interface was gradually purified. The Ni3Si layer and the MC precipitates disappeared when the Cr addition increased to 30 wt% and an interface was clearly presented with the 'gamma' phases on both sides epitaxially growing on some extent. After 200 thermal fatigue cycles, the total crack lengths were measured, which decreased with increasing Cr addition, indicating that the thermal fatigue resistance was improved. (C) 2017 Elsevier B.V. All rights reserved.
部门归属[wang, d. ; chen, x. g. ; xie, y. j.] jiangxi acad sci, inst appl phys, nanchang 330029, jiangxi, peoples r china ; [wang, w. q.] nanchang univ, sch mech & elect engn, nanchang 330031, jiangxi, peoples r china ; [chi, c. t. ; wang, m. s. ; han, x. ; xie, y. j.] chinese acad sci, inst met res, shenyang 110016, liaoning, peoples r china
关键词Vacuum Brazecoating Single Crystal Superalloy Interface Purification Thermal Fatigue Cycling Nicr-cr3c2 Coating
学科领域Materials Science, Coatings & Films ; Physics, Applied
收录类别SCI
语种英语
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/79085
专题中国科学院金属研究所
通讯作者Xie, YJ (reprint author), Jiangxi Acad Sci, Inst Appl Phys, Nanchang 330029, Jiangxi, Peoples R China.; Xie, YJ (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China.
推荐引用方式
GB/T 7714
Wang, D.,Wang, W. Q.,Chen, X. G.,et al. Influence of Cr addition on the interface purification of vacuum brazed NiCr-Cr3C2 coatings on single crystal superalloy[J]. ELSEVIER SCIENCE SA,2017,325:200-209.
APA Wang, D..,Wang, W. Q..,Chen, X. G..,Chi, C. T..,Wang, M. S..,...&Xie, YJ .(2017).Influence of Cr addition on the interface purification of vacuum brazed NiCr-Cr3C2 coatings on single crystal superalloy.ELSEVIER SCIENCE SA,325,200-209.
MLA Wang, D.,et al."Influence of Cr addition on the interface purification of vacuum brazed NiCr-Cr3C2 coatings on single crystal superalloy".ELSEVIER SCIENCE SA 325(2017):200-209.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Wang, D.]的文章
[Wang, W. Q.]的文章
[Chen, X. G.]的文章
百度学术
百度学术中相似的文章
[Wang, D.]的文章
[Wang, W. Q.]的文章
[Chen, X. G.]的文章
必应学术
必应学术中相似的文章
[Wang, D.]的文章
[Wang, W. Q.]的文章
[Chen, X. G.]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。