题名: Solidification characteristics and segregation behavior of a P-containing Ni-Fe-Cr-based alloy
作者: Wang, Changshuai;  Su, Haijun;  Guo, YongAn;  Guo, Jianting;  Zhou, Lanzhang
发表日期: 2017-9-1
摘要: Solidification characteristics and segregation behavior of a P-containing Ni-Fe-Cr-based alloy, considered as boiler and turbine materials in 700 degrees C advanced ultra-supercritical coal-fired power plants, have been investigated by differential thermal analysis and directional solidification quenching technique. Results reveal that P decreases the solidus temperature, but only has negligible influence on liquidus temperature. After P was added, the solidification sequence has no apparent change, but the width of the mushy zone increases and dendritic structures become coarser. Moreover, P increases the amount and changes the morphology of MC carbide. Energy-dispersive spectroscopy analysis reveals that P has obvious influence on the segregation behavior of the constitute elements with equilibrium partition coefficients (k(i)) far away from unity, whereas has negligible effect on the constituent elements with k(i) close to unity and has more influence on the final stage of solidification than at early stage. The distribution profiles reveal that P atoms pile up ahead of the solid/liquid (S/L) interface and strongly segregate to the interdendritic liquid region. The influence of P on solidification characteristics and segregation behavior of Ni-Fe-Cr-based alloy could be attributed to the accumulation of P ahead of the S/L interface during solidification.
刊名: SPRINGER
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Wang, Changshuai,Su, Haijun,Guo, YongAn,et al. Solidification Characteristics And Segregation Behavior Of A P-containing Ni-fe-cr-based Alloy[J]. Springer,2017,123(9):-.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Wang, Changshuai]'s Articles
 [Su, Haijun]'s Articles
 [Guo, YongAn]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Wang, Changshuai]‘s Articles
 [Su, Haijun]‘s Articles
 [Guo, YongAn]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace