题名: Ripening behavior of M23C6 carbides in P92 steel during aging at 800 degrees C
作者: Yang, Xu;  Liao, Bo;  Xiao, Fu-ren;  Yan, Wei;  Shan, Yi-yin;  Yang, Ke
发表日期: 2017-8-1
摘要: The rapid coarsening of the M23C6 carbides has been held responsible for the creep fracture in 9-12Cr martensitic heat resistant steels. A commercial P92 steel was subjected to thermal aging at a high temperature of 800 degrees C to investigate the ripening behavior of the M23C6 carbides. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were employed to characterize the microstructure evolution, especially the ripening process of the M23C6 carbides. The new concept of the effective mean size, dependent on the critical radius, was introduced to correct the measured mean size and then the Ostwald theory was applied to describe the ripening behavior of the M23C6 carbides. The ripening of the M23C6 carbides was revealed to he grain boundary diffusion controlled.
刊名: JOURNAL IRON STEEL RESEARCH EDITORIAL BOARD
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Yang, Xu,Liao, Bo,Xiao, Fu-ren,et al. Ripening Behavior Of M23c6 Carbides In P92 Steel During Aging At 800 Degrees C[J]. Journal Iron Steel Research Editorial Board,2017,24(8):858-864.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Yang, Xu]'s Articles
 [Liao, Bo]'s Articles
 [Xiao, Fu-ren]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Yang, Xu]‘s Articles
 [Liao, Bo]‘s Articles
 [Xiao, Fu-ren]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace