Combined strengthening from nanotwins and nanoprecipitates in an iron-based superalloy

IMR OpenIR

	Combined strengthening from nanotwins and nanoprecipitates in an iron-based superalloy
	Zhang, BB; Yan, FK; Zhao, MJ; Tao, NR; Lu, K; Tao, NR (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Liaoning, Peoples R China.
	2018-06-01
发表期刊	ACTA MATERIALIA
ISSN	1359-6454
卷号	151 页码:310-320
摘要	A bulk nanostructured solutionized iron-based superalloy consisting of nanotwins and dislocation structures was prepared by means of dynamic plastic deformation at a high strain rate. The nanotwins constitute similar to 51% in volume with the average twin/matrix lamella thickness of similar to 20 nm. The sample exhibits a yield strength as high as 1130 MPa but with nearly zero uniform elongation. Subsequent peak-aging treatment at 700 degrees C for 1 h results in the precipitation of nano-sized gamma prime phases with a random distribution in the nanotwins and deformed matrix. The nanotwins still remain and keep the corresponding strengthening after aging. Those dispersed nanoprecipitates further raise the strength of the aged sample to 1420 MPa. Meanwhile, the uniform elongation increases to similar to 3% due to the intrinsic plasticity of nanotwins with a reduced dislocation density after aging annealing. This kind of combined strengthening from both nanotwins and precipitates provides a new strategy to further raise the strength of nanotwinned materials or precipitation-strengthened materials. (C) 2018 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.; A bulk nanostructured solutionized iron-based superalloy consisting of nanotwins and dislocation structures was prepared by means of dynamic plastic deformation at a high strain rate. The nanotwins constitute similar to 51% in volume with the average twin/matrix lamella thickness of similar to 20 nm. The sample exhibits a yield strength as high as 1130 MPa but with nearly zero uniform elongation. Subsequent peak-aging treatment at 700 degrees C for 1 h results in the precipitation of nano-sized gamma prime phases with a random distribution in the nanotwins and deformed matrix. The nanotwins still remain and keep the corresponding strengthening after aging. Those dispersed nanoprecipitates further raise the strength of the aged sample to 1420 MPa. Meanwhile, the uniform elongation increases to similar to 3% due to the intrinsic plasticity of nanotwins with a reduced dislocation density after aging annealing. This kind of combined strengthening from both nanotwins and precipitates provides a new strategy to further raise the strength of nanotwinned materials or precipitation-strengthened materials. (C) 2018 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
部门归属	[zhang, b. b. ; yan, f. k. ; zhao, m. j. ; tao, n. r. ; lu, k.] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, liaoning, peoples r china ; [zhang, b. b.] univ chinese acad sci, beijing 100049, peoples r china
关键词	High Electrical-conductivity Dynamic Plastic-deformation Austenitic Stainless-steel Low-carbon Steels Cu-al Alloy Cr-zr Alloy Microstructural Evolution Tensile Behavior Pure Nickel Ag Alloy
学科领域	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
资助者	National Natural Science Foundation of China [51771196, 51501191, U1730140]; National Key R&D Program of China [2017YFA0204401, 2017YFA0204402]; Key Research Program of Frontier Science, Chinese Academy of Sciences
收录类别	SCI
语种	英语
WOS记录号	WOS:000432760300029
引用统计	被引频次：75[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/79290
专题	中国科学院金属研究所
通讯作者	Tao, NR (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Liaoning, Peoples R China.
推荐引用方式 GB/T 7714	Zhang, BB,Yan, FK,Zhao, MJ,et al. Combined strengthening from nanotwins and nanoprecipitates in an iron-based superalloy[J]. ACTA MATERIALIA,2018,151:310-320.
APA	Zhang, BB,Yan, FK,Zhao, MJ,Tao, NR,Lu, K,&Tao, NR .(2018).Combined strengthening from nanotwins and nanoprecipitates in an iron-based superalloy.ACTA MATERIALIA,151,310-320.
MLA	Zhang, BB,et al."Combined strengthening from nanotwins and nanoprecipitates in an iron-based superalloy".ACTA MATERIALIA 151(2018):310-320.