题名: Effect of polishing process on corrosion behavior of 308L stainless steel in high temperature water
作者: Ma, C;  Han, EH;  Peng, QJ;  Ke, W
发表日期: 2018-6-1
摘要: Effect of change in surface composition and roughness by different polishing processes on corrosion of 308L stainless steel in high temperature water was investigated. The investigation was conducted by comparing the corrosion behavior of electropolished specimens with that of the 40 nm-colloidal silica slurry polished specimens. The result revealed that the electropolished specimens had a higher corrosion rate than the colloidal silica slurry polished specimens, which was attributed to formation of an amount of chromium hydroxide and higher roughness of the electropolished surface. Moreover, the ferrite in 308L stainless steel was found to have a higher resistance to corrosion than the austenite matrix. (C) 2018 Elsevier B.V. All rights reserved.
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.

Recommended Citation:
Ma, C,Han, EH,Peng, QJ,et al. Effect Of Polishing Process On Corrosion Behavior Of 308l Stainless Steel In High Temperature Water[J]. Applied Surface Science,2018,442:423-436.

SCI Citaion Data:
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Ma, C]'s Articles
 [Han, EH]'s Articles
 [Peng, QJ]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Ma, C]‘s Articles
 [Han, EH]‘s Articles
 [Peng, QJ]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to  Add to Digg  Add to Reddit 
所有评论 (0)
内 容:
Email:  *
验证码:   刷新
标 题:
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.



Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace