Influence of the secondary phase on micro galvanic corrosion of low carbon bainitic steel in NaCl solution

IMR OpenIR

	Influence of the secondary phase on micro galvanic corrosion of low carbon bainitic steel in NaCl solution
	Wei, J; Dong, JH; Zhou, YT; He, XY; Wang, CG; Ke, W; Dong, JH (reprint author), Chinese Acad Sci, Inst Met Res, 62 Wencui Rd, Shenyang 110016, Liaoning, Peoples R China.
	2018-05-01
发表期刊	MATERIALS CHARACTERIZATION
ISSN	1044-5803
卷号	139 页码:401-410
摘要	The corrosion behavior of lath bainitic and granular bainitic steels in 0.01 mol/L NaCl solution was studied by SEM and TEM observation, electrochemical monitoring and weight loss test. The results indicate that the micro galvanic couple forms between the steel matrix and the secondary phase, which causes non-uniform micro corrosion on surfaces of two steels. In lath bainitic steel, the secondary phase omega acts as the micro anode. While in granular bainitic steel, the secondary phase M acts as the micro cathode. Moreover, the corrosion acceleration caused by micro galvanic couple is obvious in the initial immersion stage, and then it becomes weak during the long term corrosion.; The corrosion behavior of lath bainitic and granular bainitic steels in 0.01 mol/L NaCl solution was studied by SEM and TEM observation, electrochemical monitoring and weight loss test. The results indicate that the micro galvanic couple forms between the steel matrix and the secondary phase, which causes non-uniform micro corrosion on surfaces of two steels. In lath bainitic steel, the secondary phase omega acts as the micro anode. While in granular bainitic steel, the secondary phase M acts as the micro cathode. Moreover, the corrosion acceleration caused by micro galvanic couple is obvious in the initial immersion stage, and then it becomes weak during the long term corrosion.
部门归属	[wei, jie ; dong, junhua ; zhou, yangtao ; he, xiaoyan ; wang, changgang ; ke, wei] chinese acad sci, inst met res, 62 wencui rd, shenyang 110016, liaoning, peoples r china
关键词	Low-alloy Steel Bottom Plate Environment Cargo Oil Tank Mechanical-properties Pitting Corrosion Mns Inclusions Stainless-steel In-situ Microstructure Behavior
学科领域	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering ; Materials Science, Characterization & Testing
资助者	National Natural Science Foundation of China [51501201]
收录类别	SCI
语种	英语
WOS记录号	WOS:000431469300043
引用统计	被引频次：69[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/79323
专题	中国科学院金属研究所
通讯作者	Dong, JH (reprint author), Chinese Acad Sci, Inst Met Res, 62 Wencui Rd, Shenyang 110016, Liaoning, Peoples R China.
推荐引用方式 GB/T 7714	Wei, J,Dong, JH,Zhou, YT,et al. Influence of the secondary phase on micro galvanic corrosion of low carbon bainitic steel in NaCl solution[J]. MATERIALS CHARACTERIZATION,2018,139:401-410.
APA	Wei, J.,Dong, JH.,Zhou, YT.,He, XY.,Wang, CG.,...&Dong, JH .(2018).Influence of the secondary phase on micro galvanic corrosion of low carbon bainitic steel in NaCl solution.MATERIALS CHARACTERIZATION,139,401-410.
MLA	Wei, J,et al."Influence of the secondary phase on micro galvanic corrosion of low carbon bainitic steel in NaCl solution".MATERIALS CHARACTERIZATION 139(2018):401-410.