Corrosion of Fe-Ni-Cr alloys with various aluminum additions in a carburizing-oxidizing atmosphere at 900 degrees C

IMR OpenIR

	Corrosion of Fe-Ni-Cr alloys with various aluminum additions in a carburizing-oxidizing atmosphere at 900 degrees C
	Liu, S; Shen, J; Guo, XH; Liu, LL; Niu, Y; Niu, Y (reprint author), Univ Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China.
	2018-05-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	135 页码:67-77
摘要	The corrosion behavior of Fe-19Ni-13/21Cr-xAl (x = 0, 2, 6 at.%) alloys in a carburizing-oxidizing atmosphere was compared with that in a purely carburizing atmosphere at 900 degrees C. The presence of oxygen did not improve the corrosion resistance of the two alloys Fe-19Ni-13Cr-xAl (x = 0, 2 at.%), while oxygen reduced the carbon attack significantly for the other alloys. The extent of the carbon attack decreased with the increase of the aluminum content, except for the addition of 2 at.% Al to Fe-19Ni-13Cr, which did not reduce the carbon attack. Addition of sufficient aluminum promoted the formation of external Cr2O3.; The corrosion behavior of Fe-19Ni-13/21Cr-xAl (x = 0, 2, 6 at.%) alloys in a carburizing-oxidizing atmosphere was compared with that in a purely carburizing atmosphere at 900 degrees C. The presence of oxygen did not improve the corrosion resistance of the two alloys Fe-19Ni-13Cr-xAl (x = 0, 2 at.%), while oxygen reduced the carbon attack significantly for the other alloys. The extent of the carbon attack decreased with the increase of the aluminum content, except for the addition of 2 at.% Al to Fe-19Ni-13Cr, which did not reduce the carbon attack. Addition of sufficient aluminum promoted the formation of external Cr2O3.
部门归属	[liu, s.] foshan univ, coll mat sci & energy engn, foshan 528000, guangdong, peoples r china ; [liu, s. ; shen, j. ; guo, x. h. ; liu, l. l. ; niu, y.] univ chinese acad sci, inst met res, shenyang 110016, liaoning, peoples r china ; [liu, l. l.] live working ctr state grid corp hunan, changsha 410000, hunan, peoples r china
关键词	Internal Oxidation External Oxidation Transition Mechanism Resistant Behavior Kinetics Steels Nickel Scales
学科领域	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
资助者	NSFC [51371183, 51671203]
收录类别	SCI
语种	英语
WOS记录号	WOS:000429513700006
引用统计	被引频次：11[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/79336
专题	中国科学院金属研究所
通讯作者	Niu, Y (reprint author), Univ Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China.
推荐引用方式 GB/T 7714	Liu, S,Shen, J,Guo, XH,et al. Corrosion of Fe-Ni-Cr alloys with various aluminum additions in a carburizing-oxidizing atmosphere at 900 degrees C[J]. CORROSION SCIENCE,2018,135:67-77.
APA	Liu, S,Shen, J,Guo, XH,Liu, LL,Niu, Y,&Niu, Y .(2018).Corrosion of Fe-Ni-Cr alloys with various aluminum additions in a carburizing-oxidizing atmosphere at 900 degrees C.CORROSION SCIENCE,135,67-77.
MLA	Liu, S,et al."Corrosion of Fe-Ni-Cr alloys with various aluminum additions in a carburizing-oxidizing atmosphere at 900 degrees C".CORROSION SCIENCE 135(2018):67-77.